Fabrication of YBaCuO junctions by the irradiation of focused ionbeam.
スポンサーリンク
概要
- 論文の詳細を見る
We have fabricated Josephson junctions in YBa2Cu3 O7-δ (YBaCuO) thin films by the irradiation of focused ion beam (FIB). We used Be2+ ions with the energy of 200 keV. When the fluence of Be2+ ions was 1.2×1016 ions/cm2, the I-V characteristics of the junctions at 4.2 K showed RSJ-like characteristics with the excess current. The IcRn product of the junctions was 1.1 mV at 6.3 K. Shapiro steps up to 20th step could be observed by the irradiation of 8.47 GHz microwave at 6.3 K. The magnetic modulation curve of the junction at 4.2 K was similar to the Fraunhofer pattern. These characteristics remained unaltered after preservation in a desiccator for 6 months
- Institute of Electrical and Electronics Engineersの論文
著者
-
SOUTOME Yoshihisa
Advanced Research Laboratory, Hitachi Ltd.
-
Okabe Y
Univ. Tokyo Tokyo Jpn
-
Soutome Y
Advanced Research Laboratory Hitachi Ltd.
-
Shiga H
Univ. Tokyo Tokyo Jpn
関連論文
- Electrical Properties of La-Sr-Cu-O/Al Contact
- Circuit Simulation Study for Characterization of High-Temperature Superconducting Sigma-Delta Modulator with 100 GHz Sampling(Special Issue on Superconductor Digital/Analog Circuit Technologies)
- HTS Surface-Modified Junctions with Integrated Ground-Planes for SFQ Circuits(Special Issue on Superconductive Electronics)
- Y-BA-CU-O THIN-FILMS BY EVAPORATING THE 3 ELEMENTS USING RESISTIVE HEATING
- Stochastic Resonance in the Hodgkin-Huxley Network
- Fabrication of YBaCuO junctions by the irradiation of focused ionbeam.
- Characterization of YBa_2Cu_3O_ Co-planar Josephson Junctions Using Focused Ion Beam(Special Issue on Superconductive Electron Devices and Their Applications)
- Co-planar Josephson Junction Using Nonsuperconductive YBaCuO Formed on Very Locally Damaged Substrate by FIB
- The Effects of Active Oxygen Atoms in Y-Ba-Cu-O Sputtering