117104 AZ31マグネシウム合金の塑性加工に及ぼす組織の影響(一般01 材料科学・材料力学1)

概要

論文の詳細を見る
To improve the plastic formability of AZ31Mg alloys, this study examined the relation between mechanical properties such as plastic workability and changes of structural refinement after the multi-axial alternative warm forging (MAF) and roll working with recrystallization heat treatment or high-temperature heat treatment. In MAF, work pieces were rotated through 90° on the longitudinal axis between each forging press. This procedure was successful to be introduced large strain into materials. Rolling condition was total redaction 50%, temperature 493K, and water quench. The plastic formability assessment was carried out by conical cup test at testing speed 10mm/min under temperature (293-523K). It was found that at test temperature 423K, AZ31Mg formability was more than those of A5083 at all process. Especially, AZ31Mg alloys with high-temperature heat treatment had good conical cup values at room temperature to close to those of A5083.
一般社団法人日本機械学会の論文
2011-03-17