1124 プラズマ窒化を施したFe-C-Mn鋼の疲労特性に及ぼすMn添加量の影響(OS11-6 材料の疲労挙動と損傷評価-表面処理・締結材-)

概要

論文の詳細を見る
Rotating bending fatigue tests were conducted for a series of plasma-nitrided Fe-C-Mn steels in order to investigate the effect of manganese contents. 5 types of steels were prepared, i.e., 0.0Mn, 0.5Mn, 1.0Mn, 2.0Mn and 4.0Mn. Microstractures of the steels were fenite-pearlite except 4.0Mn whose microstructure was martensite. 2.0Mn and 4.0Mn of the nittided specimens had a hardened layer of 0.5 to 1 mm in depth, while the no hardening was observed in 0.0Mn, 0.5Mn and 1.0Mn of the nitrided specimens. In case of 0.0Mn, 0.5Mn and 1.0Mn, the nitrided specimen showed surface fracture and increase of fatigue strength was veiy small. The 2.0Mn nitrided specimen showed surface fracture and fatigue strength were largely improved by plasma-nilriding. On the other hand, in case of 4.0Mn, the nittided specimen showed internal fracture beneath the hardened layer and the fatigue strength were lower than that of the 2.0Mn nitrided specimen.