Fundamental Study of Glass-Metal Bonding
スポンサーリンク
概要
- 論文の詳細を見る
A fundamental study of glass to metal bonding with the glasses of the systems Na_2O-SiO_2 and K_2O-SiO_2 and nickel was performed. From the result of bond strength, it was suggested that no difference between each bond strength was observed when the oxide film with proper thickness was preliminary formed at the surface of nickel metal. Further, it was suggested that it seems desirable to use soda-aluminosilicate glass as dental materials from the results of thermal expansivity, solution durability to distilled water and higher adherence strength. With X-ray diffraction analysis, the compound regarding as Na_6Si_8O_<19> was found in the 3Na_2O・7SiO_2 glass-nickel bonding at 700℃. Further investigation is necessitated because it remains unclear whether this compound is harmful or not.
- 大阪大学の論文
著者
-
IWAMOTO Nobuya
Osaka University
-
MAKINO Yukio
Osaka University
-
Wada Hiroki
Wada Precision Dental Laboratries Ltd.
-
KARINO Sei-ichi
Wada Precision Dental Laboratries Ltd.
-
AWAJI Toshio
Wada Precision Dental Laboratries Ltd.
関連論文
- Heat of Fusion of Barium Fluoride by Cryoscopic Measurement
- Melting Points of Inorganic Fluorides
- Structural Investigation of Glass System Na_2O-Ga_2O_3-SiO_2
- Wetting Phenomena at High Temperature (Part II)
- Wetting Phenomena at High Temperature-Part 1
- Electric Field Assisted Treatment of Various Plasma Sprayed ZrO_2 Coatings(Physics, Process, Instruments & Measurements)
- Fundamental Considerations on Plasma Sprayed Ceramic Coating (Report IV) : Effects of Mullite Addition on Alumina
- Fundamental Considerations on Plasma Sprayed Ceramic Coating (Report III) : Effects of Zircon Addition on Zirconia
- Fundamental Considerations on Plasma Sprayed Ceramic Coating (Report I) : Problems of Plasma Sprayed Zirconia
- Characterization of Titanium Compound Films Deposited by Plasma-CVD