Anelastic Relaxations of La-based Amorphous Alloys

概要

論文の詳細を見る
The relaxation processes of La-based amorphous alloys with distinct glass transition phenomenon have been investigated in the temperature regions around the glass transition temperature and well below the glass transition temperature by the dynamic mechanical measurements. The amorphous alloys used in this study are La_<55>Al_<45-x>Ni_x (x=0 to 35 %) and La_5Al_<85>Ni_<10> alloys for examination of the compositional effect and La_<55>Al_<25>M_<20> (M=Cu, Pd or Au) alloys for the substitutional effect. The sub-T_g relaxation phenomenon was observed for La_<55>Al_<45-x>Ni_x (x=5 to 35 %) and La_5Al_<85>Ni_<10> amorphous alloys. The relaxation due to the glass transition was recognized for La_<55>Al_<45-x>Ni_x (x=0 to 35 %), La_5Al_<85>Ni_<10> and La_<55>Al_<25>M_<20> (M=Cu, Pd or Au) amorphous alloys. In addition, the second-stage relaxation in the glass transition region was also observed for La_<55>Al_<45-x>Ni_x (x=15 to 30 %) and La_<55>Al_<25>M_<20> (M=Cu, Pd or Au) amorphous alloys with a wide supercooled liquid region exceeding 35 K. The appearance of the two kinds of relaxation units seems to reflect the difference in the chemical bonding nature among the constituent elements.
東北大学の論文
1992-03-25