Constitution of the Indium-Rich Portion of the Indium-Magnesium System
スポンサーリンク
概要
- 論文の詳細を見る
The equilibrium phase diagram of the indium-magnesium system in the range up to 40 at.% Mg has been established by X-ray diffraction and thermal analysis. The solid-solubility of magnesium in indium does not exceed about 5 at.%. An intermediate solid solution, γ, with a face-centered cubic structure exists over a wide range of composition. An ordered phase, γ', with superstructure of Cu_3Au-type, is formed near 28 at.% Mg at temperatures below 114℃. The axial ratio c/a of the primary solid solution of indium in magnesium changes as a function of electron/atom ratio as in the parallel case of the indium-cadmium system. Reasons are advanced to explain the conflict between the present results and those of earlier investigators.
- 東北大学の論文
著者
-
HIRABAYASHI M.
The Research Institute for Iron, Steel and Other Metals, Tohoku University
-
Koiwa M.
The Research Institute For Iron Steel And Other Metals
-
Koiwa M.
The Research Institute For Iron Steel And Othdr Metals Tohoku University
-
HIRAGA K.
The Research Institute for Iron, Steel and Other Metals
-
Hiraga K.
The Research Institute For Iron Steel And Other Metals
関連論文
- Stress-Strain Analysis of Single Cubic Crystals and Its Application to the Ordering of CuAu I : Paper II
- An Experimental Study on the Ordered Alloy Ni_2Cr
- A Theory of Internal Friction Peak Due to Thermal Unpinning of Dislocations and Its Application to P_1 Peak in Copper
- Age-Hardening of Aluminium-Gold Alloys
- Constitution of the Indium-Rich Portion of the Indium-Magnesium System
- Theory of Internal Friction due to Diffusing Particles in Multiwell Potentials
- Theory of the Snoek Effect in Ternary B.C.C. Alloys : I. General Theory
- On the Validity of Chemical Reaction Scheme in the Treatment of the Behaviour of Point Defects
- A New Type of Long Period Superlattice with Hexagonal Symmetry in Au-Cd Alloys
- Vacancy Ordering in Vanadium Carbides Based on V_6C_5
- Theory of the Snoek Effect in Ternary B.C.C. Alloys : IV. CsCl Type Lattice
- Long-Period Ordered Structures in the Quasi-Binary CO_3V-Ni_3V Alloy