Evaluation of Cryogenic Fracture and Damage Properties of GFRP Compact Tension Specimens

概要

論文の詳細を見る
This paper describes an experimental and analytical study on fracture and damage behavior of GFRP woven laminates at cryogenic temperatures. CT (compact tension) tests were carried out at room temperature, liquid nitrogen temperature (77 K) and liquid helium temperature (4 K) to evaluate the critical values of the fracture mechanics parameters. During the CT tests, AE (acoustic emission) method was implemented. AE signals can identify the critical load at which gross failure occurs. A FEA (finite element analysis) was also done to calculate the fracture mechanics parameters. The failure criteria (Hoffman criterion and maximum strain criterion) or the damage variable based on the continuum damage mechanics was incorporated into the model to interpret the experimental measurements and to study the damage distributions within the specimen. Several methods of calculating J-integral are discussed.