Fine Structure of As-Quenched Omega-Phase of Ti-Mo Alloy Observed by HREM with Image Processing
スポンサーリンク
概要
- 論文の詳細を見る
The structure of the omega-phase which is formed by the quenching of Ti-14 wt%Mo alloy from 1223 K to 273 K was investigated at the atomic level using a high-resolution electron microscope (HREM). The HREM image were formed by using 15 diffracted waves including diffuse scattering due to the omega-phase. The focus of imaging was adjusted to aberration-free-focus (AFF) condition and the observed images were processed by a computer to reveal the structure of the omega-phase only. It was found that the omega-phase co-exists with an omega-like structure formed by vacancy clusters.
- 社団法人応用物理学会の論文
- 1987-06-20
著者
-
Hida M
Okayama Univ. Okayama Jpn
-
Hida Moritaka
Faculty Of Engineering Okayama University
-
Hashimoto Hatsujiro
Faculty Of Engineering Okayama University Of Science
-
Sukedai Eiichi
Faculty Of Engineering Okayama University Of Science
関連論文
- EXAFS Study on the Local Structure of a New High-T_c Superconductor in the Bi-Sr-Ca-Cu-O System : Electrical Properties of Condensed Matter
- EXAFS Studies on Y_Ba_xCuO_Superconductors
- High-Resolution Transmission Electron Microscopic Observation of Stacking Faults in Fe-35 mol%Al Alloy with Ordered B2 Structure
- Morphology and structure of various phases at the bonding interface of Al/steel formed by explosive welding
- Phase Transformation of α" Martensite Structure by Aging in Ti-8mass%Mo Alloy
- Tensile Behavior and Cold Workability of Ti-Mo Alloys
- Wide Range Observation on Crystal Zone of Single Variant of R-phase and Martensite in Ti-50.4 at%Ni Alloy
- Evaluation of Bonding State of BCC(Fe) Edge Dislocation Core by DV-Xα Cluster Method
- TEM observation of the α"→β inverse transformation in Ti-40mass%Nb alloy (日本電子顕微鏡学会第46回シンポジウム 材料のナノ・生物のナノ) -- (ポスターセッション "7th International Symposium on Advanced physical Fields(APF-7)"との合同セッション)
- Solid Solubility and Transformation in Mechanically Alloyed Ti-Mg Powders
- A Stable High-Brightness Electron Gun with Zr/W-tip for Nanometer Lithography. : I. Emission Properties in Schottky- and Thermal Field-Emission Regions
- Fine Structure of As-Quenched Omega-Phase of Ti-Mo Alloy Observed by HREM with Image Processing
- Growth Behaviour of Athermal ω-Phase Crystals in Ti-15mass%Mo Alloy Studied by In-situ Dark Field and High Resolution Electron Microscopy
- Changes of Volume and Surface Compositions of Polymethylmethacrylate under Electron Beam Irradiation in Lithography