Electronmicroscopic Observation of Print-Out Effect on AgBr Crystals Obtained from Low Sensitive Photographic Plate
スポンサーリンク
概要
- 論文の詳細を見る
The print-out effects due to xenon light illumination were studied electronmicroscopically in the temperature range from room temperature to 250℃ on comparatively perfect silver bromide crystals obtained from the low sensitive photographic plate. As a result, it was found that a few pits appeared on the edges of the grains differing from the case of the grains obtained from the SSS photographic film already reported^<1)>. Triangular patterns^<1,2)> hardly appeared on the grains at room temperature -250℃. Various silver protrusions bounded almost with (100) crystal surfaces appeared on the grains at 90℃-160℃. Silver whisker grew the grains at 90°-160℃ exposed to xenon light in vacuum. The whisker had two twin planes and its axis was always <110> direction, and also its crystal orientation is parallel to that of its mother crystal. It was confirmed that this whisker grew by the root growth mechanism.
- 社団法人応用物理学会の論文
- 1969-12-05
著者
-
Iijima Sumio
Research And Development Group Nec Corporation
-
Iijima Sumio
Research Institute For Scientific Measurements Tohoku University
関連論文
- Revolution in Carbon Nanotube Synthesis-"Super Growth"
- Electronmicroscopic Observation of Print-Out Effect on AgBr Microcrystals
- Fine Particles of Silicon. II. : Decahedral Multiply-Twinned Particles
- Preparation of Carbon Nanotubes by Arc-Discharge Evaporation
- Fine Particles of Silicon. I. : Crystal Growth of Spherical Particles of Si
- Electronmicroscopic Observation of Print-Out Effect on AgBr Crystals Obtained from Low Sensitive Photographic Plate
- Motion of Surface Atoms on Small Gold Particles Revealed by HREM with Real-Time VTR System
- Electronmicroscopic Observations of the Effect of Electron Irradiation and Print-Out Effect on AgBr Crystal
- Ultra-Fine Spherical Particles of γ-Alumina: Electron Microscopy of Crystal Structure and Surface Morphology at Atomic Resolution