A Topographic and Magnetic Study of Sputtered Nickel Thin Films (第4回アジア情報記録技術シンポジウム〔英文〕)

概要

論文の詳細を見る
Nickel thin films were deposited onto (100) silicon wafers using the sputtering technique. The thickness was varied between 45 to 500 nm. The nickel film formed in the initial stage (45 nm) was an uniform and continuous layer on the silicon substrate coated with a native silicon oxide layer. The film with a thickness of 78 nm exhibited high coercivity H_c (806 Oe) and high squareness in the perpendicular direction to the film plane, while H_c of 349 Oe was measured in the film plane. As the thickness increased, coercivity and magnetic anisotropy reduced and a plane anisotropy was finally exhibited in thick films (〜500 nm). TEM study showed that the films were mixtures of a columnar structure on the top and a uniform continuous structure on the bottom. All the films have shown a (111) texture and the grain size was estimated to be 15-20 nm.