試作高Cr系溶接棒による機械的冶金的性質 : 湿式水中アーク溶接に関する研究(第4報)

概要

論文の詳細を見る
In underwater welding by the use of commercial covered austenitic stainless steel electrode, the mechanical properties are not so good and the hot crack occurs in the weld metal. This study is investigated the mechanical and metallurgical properties with trial covered stainless steel electrode (RM1). The following results are obtained : (1) The compositional analysis of weld metal with RM1 rod are the same as Schaeffler's diagram (penetration 40%) using trial covered stainless steel electrode.(2) The quantity of diffusible hydrogen collected in mercury reaches to a constant volume in about 500 hr, it is about 8 ml/100 g Fe in case of RM1 rod. The hydrogen embrittlement and the delayed cracking are hard to occur because of the lower quantity of diffusible hydrogen, so the RM1 rod is adapted for the underwater welding rod.(3) The weld metal seldom has blowholes, and no cracks are observed to the weld metal in X-ray inspection.(4) The vicker's hardness in heat-affected zone is about Hv350 and that of weld metal is about Hv220 when used RM1 rod, it does not have quench hardenability in underwater welding.(5) In notched tensile test, the tensile strength of weld metal is about 660 MPa and that of bond about 645 MPa.(6) In the impact test, the RM1 rod is good for notch toughness because of the lower transition temperature.
社団法人溶接学会の論文
1987-02-05