ステンレス鋼溶接金属の低温鋭敏化に関する加速熱処理条件の検討 : オーステナイト系ステンレス鋼溶接部の低温鋭敏化とレーザ表面溶融処理によるその改善(第2報)

概要

論文の詳細を見る
The sensitization behavior in the weld metals of Type 308 stainless steel was theoretically studied in order to determine the heat-treating condition to simulate low temperature sensitization (LTS). The theoretical parameter ΔS was introduced to evaluate the amount of chromium depleted zone adjacent to the grain boundaries. Calculation of ΔS has shown that the value of ΔS increased at first and then decreased from a certain time, which was corresponding to the deterioration of intergranular corrosion resistance and its healing in the weld metal of stainless steels during sensitizing heat-treatment. Moreover, the value of ΔS was found to agree fairly well with the degree of sensitization measured by EPR test. On the basis of the results of calculating ΔS, the sensitizing condition to simulate the low temperature sensitization was considered. The typical sensitizing condition was determined 773 K×30 ks, which is corresponding to the condition of 573 K×1.26×10^9 s.
社団法人溶接学会の論文
1996-11-05