直接窒化反応法を利用したAlNの生成機構とAl-AlN複合焼結体の特性 : アルミニウム合金粉末粒子の焼結現象と粒子表面構造解析に関する研究(第3報)

概要

論文の詳細を見る
Direct nitriding process for in-situ formation of AlN has been developed by using the reaction between solid-state metallic Al and nitrogen gas after the deoxidizing reaction of the Al_2O_3 surface film by Mg contained in aluminum alloy powder particles. In-situ reacted AlN grows on the particle surface and has a layer structure with a width of 20-30 nm. A good bonding is observed at the interface between in-situ reacted AlN and the aluminum matrix of the primary particle. The Direct nitrided and sintered Al-AlN composite material shows superior mechanical properties, such as ultimate tensile strength and elongation, to the Al-AlN composite material produced by the conventional premixing process. This is because the hardening effect due to the fine AlN dispersions in the matrix and the good bonding at the interface between in-situ reacted AlN and the aluminum matrix.
社団法人溶接学会の論文
2001-05-05