Hydrogen-Induced Disbonding for Austenitic Stainless Overlay Weld Metal Exposed to Elevated Temperature under High Pressure Hydrogen Atrnosphere
スポンサーリンク
概要
- 論文の詳細を見る
- 社団法人溶接学会の論文
- 1984-10-01
著者
-
Araki T
Ehime Univ.
-
YONEDA Masafumi
Faculty of Engineering Osaka University
-
Araki T
Department Of Materials Science And Engineering Ehime University
-
Kikuta Y
Osaka University
-
Kikuta Yoneo
Faculty Of Engineering Osaka University
関連論文
- Contraction Process and RRC Test of Nodular Graphite Cast Iron Weldments : Studies on the Weld Cracking of Nodular Graphite Cast Iron (Report 5)
- Preheating Effect on the Critical Rupture Stress of Nodular Graphite Cast Iron Welds : Study on the Weld Cracking of Nodular Graphite Cast Iron (Report 2)
- Techniques to separate metal from waste printed circuit boards from discarded personal computers
- Improvement of temperature coefficient of capacitance in Y5V film capacitor prepared by pulsed laser deposition (特集 [日本材料科学会]支部特集(四国地区))
- Pulverization of waste printed circuit boards
- Formation of Droplets on Thin Film Surface in Pulsed Laser Deposition Using Metal Targets
- Metallurgical Study on the HAZ Embrittlement of High Strength Steel (Report 1) : Application of the Quantitative Chemical Analysis for Precipitates to Steel and its Welds
- Contribution of Cementites to Notch Toughness in Structural Steel Welds
- Effect of Nonmetallic Inclusions on Hydrogen Assisted Cracking
- Effect of Hot Strain Embrittlement on Cold Crack Sensitivity in Steel Welding
- The Effect of Center Segregation of TMCP Steels with Continuous Casting Process on Weld Cold Cracking
- The Development of BaTiO3 Thin Films for Multi Layer Ceramic Capacitor by Pulsed Laser Deposition
- Effect of Some Parameters on Microcrackings in the Fillet Weld between the Lowest Course Shell Plate and the Annular Plate in Oil Strage Tank
- Prevention of Hydrogen-Induced Disbonding for Austenitic Stainless Overlay Weld Metal
- Hydrogen-Induced Disbonding for Austenitic Stainless Overlay Weld Metal Exposed to Elevated Temperature under High Pressure Hydrogen Atrnosphere
- The Reheated Zone Toughness of Multipass Weld Metal (Report 1) : Comparison of Reheated Zone Toughness between Si-Mn System and High Strength Low Alloy System Weld Metals
- Ductility Loss due to Dynamic Strain Aging in Heat-Affected Zone of High Strength Low Alloy Steel