染色過程中に誘起されるナイロン6繊維の物性変化
スポンサーリンク
概要
- 論文の詳細を見る
The change in physical properties of nylon 6 fiber dyed with a disperse dye was investigated using stress-strain curves, dynamic viscoelastic measurements, differential scanning calorimetry, and density measurements. The initial rise and stress of the yield point, which follows the slope of initial rise of the stress-strain curve, were greater for the dyed fiber than they were for the control. At the same time, it was observed that in the case of dyed fiber, the shrinkage in fiber length which occurred during processing was suppressed more and the crystallinity increased more, compared to the control. The phenomena might be closely related to each other. The tendency mentioned above was much clearer in the case of fiber treated with a higher drawing ratio. Although the amount of dye molecules absorbed into the fiber was almost the same for all dyed specimens, the induced changes in properties varied with the drawing ratio. Therefore, it could be assumed that induced changes in properties were not only due to the existence of the dye molecules in the fiber, but also to the structural change produced during the dyeing process. When the dyed fiber was compared with the control, it was found that the temperature at which the storage modulus E' begins to drop shifted to the lower side, and a higher storage modulus existed in the rubbery elastic state. These results suggest that the dyeing treatment gives rise to a kind of structual separation in the amorphous region, that is, some amorphous regions consisting of loose packing molecules relax to a much looser packing state and some amorphous regions of close packing molecules result in a much closer, higher enthalpic packing state or crystallization. In other words, the dye molecule during the dyeing process, in cooperation with the thermal activation in the wet state, might play an important role in accelerating the moleculer movement of the polymer chain in the amorphous state and lead to structual separation as described above.
- 社団法人日本家政学会の論文
- 1996-07-15
著者
関連論文
- スカート丈およびブレザー丈の周期性について
- 新旧ファッションの認知能形成に対する思春期に経験したファッショントレンドの影響
- 布の透明性と光学的パラメータとの関係
- 紫外光照射が未染色およびC. I. Disperse Orange 3で染色したナイロン6繊維の力学的性質におよぼす影響について
- 紫外線照射したポリプロピレン単繊維のTL曲線と強伸度挙動について
- 染色したナイロン6織物の力学的性質とその官能評価
- 染色過程中に誘起されるナイロン6繊維の物性変化
- 新旧服装ファッションに関する女性の識別行動
- 織物の反射率の重ね枚数依存性について
- 分散染料で染色したポリプロピレン繊維の物性変化
- 冬の学生服地の性能(資料)
- 3年間着用後の学生服地の劣化分布
- 人体表面のかたさ特性に関する一考察
- 衣服圧に関する研究-2-異方性布の曲面変形時の圧力評価〔英文〕
- 年頭所感
- 座談会 家政学と家庭科教育との関係を考える (<視点>家庭科教育の活性化に向けて1)
- 4. 「研究」をめぐる全体会と分科会(アジア地区家政学会議と第3回韓日家政学シンポジウム参加報告)
- 衣生活におけるライフスタイルとその再認識〔含 質疑応答〕
- 60周年に当たり更なる発展を願って(名誉会員メッセージ,日本家政学会60周年記念)
- 第10回アジア地区家政学国際会議(横浜大会)(国際交流委員会,1)常置委員会・特別委員会,学会活動の回顧と展望,日本家政学会60周年記念)
- 家政学 未来への挑戦 : 全米スコッツデイル会議におけるホーム・エコノミストの選択, (社)日本家政学会家政学原論部会 翻訳・監修, 定価4,500円+税, 2002年6月発行
- 被服学(家政学会誌による家政学研究の推移・動向(1988〜1997))
- 衣服の消費と廃棄
- 被服学関係部会合同夏季セミナー報告
- 消費者問題委員会の活動報告
- 衣服の拘束性に関する研究--オ-バ-コ-トの肩部衣服圧に関するモデル的解析
- 小学校の卒業記念写真からたどる洋装化