Fretting fatigue is one of the most important phenomena for inducing a dramatic reduction of fatigue strength and consequently, of unexpected failure accidents. There are numerous works on fretting fatigue. The objective of the present review is to clarify fretting fatigue mechanisms based on the vast amount of research work. A fretting fatigue crack is initiated at the highest point of tangential force on a contact surface in the very early stage of fatigue life. The tangential force is the dominant factor in enhancing crack initiation and propagation and hence, in reducing fatigue strength. Further studies on short crack and mixed-mode crack growth behavior in fretting fatigue are needed.
- 一般社団法人日本機械学会の論文
- 1995-10-15
著者
-
Mutoh Yoshiharu
Department Of Mechanical Engineering Nagaoka Univ. Of Technology
-
MUTOH Yoshiharu
Department of Material Science, Nagaoka University of Technology
関連論文
- Time-dependent Fracture Mechanics Approach to Crack Growth of Solder
- Low Cycle Fatigue Behavior and Mechanisms of a Lead-free Solder 3.5Ag/96.5Sn(Electronic Devices)
- YBa_2Cu_3O_ Angle Grain Boundary Junction on Si Bicrystal Substrate
- Diffusion Bonding of Y-Ba-Cu-O High-T_c Superconductors
- Singularity at the Interface Edge of Bonded Transversely Isotropic Piezoelectric Dissimilar Materials
- Interface Fatigue Crack Propagation in Ceramic Thermal Barrier Coatings
- An Evaluation of the Adhesive Strength of the Interface between a Coating and Substrate
- 133 Cohesive Strength at the Interface Between Coating and Substrate
- 129 Effect of Environment on Fretting Fatigue Strength of Cast Al-Si Aluminum Alloy
- 312 CONTROL OF INTERMETALLIC PHASE FORMATION AT THE INTERFACE OF STEEL/ALMINUM DISSIMILAR METALS LASER LAP JOINT BY USING A BACKING PLATE
- Subsurface Crack Propagation in Rolling Contact Fatigue of Sintered Alloy
- 131 Subsurface Crack Propagation in Rolling Contact Fatigue of Sintered Alloy
- 514 Interface Fatigue Crack Propagation in Ceramic Thermal Barrier Coatings
- 409 Fretting Fatigue Design Curve based on Stress Distribution at the Contact Edge for Automotive steel
- On the Equivalent Thickness of a Side-Grooved Specimen
- 325 マグネシウム合金の疲労特性に及ぼす環境の影響(OS1-5 環境・高温および熱疲労)(OS1 高強度材・表面改質材の疲労と破壊)
- E-1 Thermal Shock Failure in Tungsten-10%Rhenium by Laser Irradiation Method(Session: Thermal Fatique/Creep)
- Stress Field near the Contact Edge in Fretting Fatigue Tests(Special Issue on strength and Fracture, and Experimental Mechanics)
- Effect of Relative Slip Amplitude on Fretting Fatigue Behavior of Silicon Nitride
- Mechanisms of Fretting Fatigue
- 130 Effect of Residual Stress on Fretting Fatigue Crack Propagation and Fatigue Strength
- Stress Field near the Contact Edge in Fretting Fatigue Tests(Tribology)
- Diffusion Bonding of Bi-Pb-Sr-Ca-Cu-O High-T_c Superconductors
- Stress Singularity at the Edge of Fiber/Matrix Interface
- 232 Al_2O_3-based Composite with BaTiO_3 Sintered by Spark Plasma Sintering
- J0403-3-2 Fretting Fatigue Strength Prediction of Dovetail Joint Based on Tangential Stress Range : Compressive Stress Range Diagram
- GS0304 Fretting Fatigue Strength and Life Prediction based on Stress distribution at the Contact Edge
- A Method for Determining Elastic-Plastic Stress Singularity at the Interface Edge of Bonded Power Law Hardening Materials(Stress Analysis)
- Effects of Dissolved Oxygen on Fatigue Characteristics of Austenitic Stainless Steel in 0.9wt% Sodium Chloride Solutions
- Effect of Underlay Stiffness on Cutting Profile of Polycarbonate Sheet during Wedge Indentation Process
- Failure Behavior of Sensitized SUS304 Stainless Steel with Small Surface Pre-Crack under Constant Load Condition in Simulated BWR Environment
- Fatigue Crack Growth Characteristics of Epoxy Resin Reinforced by Silica Particles at Elevated Temperature
- Dissimilar Materials Micro Welding between Stainless Steel and Plastics by Using Pulse YAG Laser
- Computational Investigation on Molten Pool of Single and Twin Beam Laser Welding
- Influence of Second Phase Particle on Fatigue Crack Growth Behavior in Ferrite Matrix Steels
- 818 STUDY ON RELIABILITY OF PB FREE Sn-Ag-Cu SOLDER JOINT