概要
- 論文の詳細を見る
The chemical form of hydrogen in lithium oxide is mainly lithium hydroxide, which is formed from the oxide and atmospheric moisture during its storage. The reaction of the hydroxide with carbon monoxide afford hydrogen gas and carbonate, so that hydrogen content in lithium oxide can be easily determined by the following method: lithium oxide sample (100 to 500 mg) is placed on a reaction tube (test-tube type, 15 mm i.d. × 200 mm, glassware). Then, carbon monoxide gas is passed through the tube at 80 ml/min and the tube is heated at 390℃ for 15 min. The hydrogen evolved from the sample is determined by using thermal conductivity detector. The evolution profile of hydrogen gas with the reaction of lithium hydroxide and carbon monoxide was influenced by physical property (density of powder) of sample rather than its hydrogen content. Carbonate in sample did not interfere with the determination of hydrogen. The lower limit of determination was 0.002 % for 500 mg of sample. The required time for analysis was about 20 min after the sample was weighed under a dried atmosphere in gloved box. The standard deviations for the determination of 0.028 %, 0.18%, and 0.70% of hydrogen were 0.004 %, 0.01 %, and 0.05 %, respectively.
- 社団法人日本分析化学会の論文
- 1984-04-05
著者
関連論文
- 一酸化炭素キャリヤーガス法による酸化リチウム中の不純物水素の迅速定量
- アルカリ融解・二酸化炭素発生-重量法による炭化ケイ素中の全炭素の定量
- 不活性ふんい気において酸化鉛(IV)、酸化銅(II)または硫酸バリウムを酸化剤とする無定形炭素及び一炭化ウラン中の炭素の定量
- 不活性ガス抽出・重量法による水素化ジルコニウム及びウラン-水素化ジルコニウム中の水素の定量
- 硫酸バリウムを酸化剤とする炭素定量法