608 熱遮蔽セラミックコーティングの界面はく離挙動に及ぼす熱時効処理の影響

概要

論文の詳細を見る
Knowledge of the degradation mode in thermal barrier coatings (TBCs) is a prerequisite for the prediction of their remaining life of gas turbine blades. This paper describes the effects of thermal aging on the microstructure in a YSZ-based thermal barrier coating system deposited on Ni based superalloy substrates. The heat treatment of the TBC specimens were conducted at 1373K for 100h, 500h and 1000h in air for thermal aging. The thermally aged coating system had thermally grown oxide (TGO) layer between the substrate and the TBC. TGO consisted of not only alumina but also other oxides. This oxide layer that named mixed oxides (MO) is composed of Ni, Co, Cr and O. 4 point bending tests were carried out in order to evaluate the TBC/substrate interface strength. The interface strength depended on the period of thermal aging in both type of tests. The interface strength increased initially up to the aging time of 100h, and then decreased drastically for the longer aging time. In 4 point bending tests, crack propagated along the interface between TBC and substrate. These results suggested that the interface strength depended on not only the formation of oxides but also the fracture properties of the top coatings.
一般社団法人日本機械学会の論文
2002-09-20