1007 曲げ試験による熱遮蔽コーティングのはく離挙動評価
スポンサーリンク
概要
- 論文の詳細を見る
To develop the life evaluation method for Thermal Barrier Coating (TBC) used in gas turbine high temperature parts, the damage factors and damage patterns were discussed. In TBC system mechanical damages, such as vertical crack, delamination and erosion, arise from mechanical, thermal and residual stresses. And chemical damages, such as thermally grown oxidation, arise from high temperature gaseous environment. Considering the stress distribution in TBC during stop operation of gas turbine, 4 point bending tests were performed to evaluate the delamination strength. And the effect of exposure in high temperature environment on the delamination strength was observed.
- 社団法人日本機械学会の論文
- 2003-09-19
著者
関連論文
- 829 携帯機器用 CSP はんだ接続部の信頼性評価
- 携帯電子機器BGAはんだ接続部の疲労強度
- 427 ガスタービン動翼の長寿命化へ及ぼす再生処理の効果(余寿命と寿命延伸,高温機器・材料の損傷検出・評価・余寿命推定,オーガナイスドセッション2)
- 808 構造物の微細化や薄型化が BGA 接続寿命に及ぼす影響
- 21313 振動試験機を用いたガスタービン動翼の振動特性評価(材料強度と構造設(1),OS.5 材料強度と構造設計)
- タービン動翼の振動特性に及ぼす拘束力の影響
- 1007 曲げ試験による熱遮蔽コーティングのはく離挙動評価
- 305 異方性を有する Ni 基一方向凝固材の低サイクル疲労寿命および振動挙動
- 409 Ni基超合金MM247の疲労寿命に及ぼす鋳造組織の影響(OS3-2 疲労,OS3 エネルギー構造機器の健全性評価と信頼性の高度化3)
- 2218 Ni基鍛造材,鋳造材からなる摩擦圧接材の強度へ及ぼす微視組織の影響(J10-3 溶接接合強度評価,J10 締結・接合部の力学とプロセス)
- 304 力学的な予損傷を与えられた CrMoV 鋼におけるクリープ, 疲労き裂進展速度
- 408 Ni 基超合金一方向凝固材のクリープ疲労き裂進展挙動に対する酸化の影響
- 843 Sn-Ag-Cu 系はんだ BGA 接合部の疲労強度評価
- 1116 Sn-Ag-Bi-Cu系Pbフリーはんだの機械的性質と低サイクル疲労強度(OS-1 鉛フリ-はんだ)
- タービン動翼の振動特性に及ぼす拘束力の影響
- 304 熱機械疲労下における熱遮蔽コーティングのはく離挙動に及ぼす長期運用の影響(OS2-1 皮膜・薄膜のき裂・界面き裂,OS2 薄膜・皮膜とその膜構造の特性評価)
- 熱機械疲労下における熱遮蔽コーティングのはく離挙動
- 701 応力集中源を複数有するNi基単結晶超合金の低サイクル疲労強度(エネルギー・発電プラント機器,一般セッション)
- 511 複数の微小孔を有するNi基一方向凝固超合金の高温低サイクル疲労寿命評価法(クリープ疲労・熱疲労,高温強度に影響する諸因子,オーガナイスドセッション2)
- 中沢メソッドを用いたガスタービン圧縮機ダブテール溝形状の最適化手法の検討(日本ガスタービン学会創立40周年記念特集)
- 205104 Ni基鍛造合金の疲労き裂発生寿命に及ぼす耐酸化コーティングの長寿命化効果(OS04 材料・機械・構造物における強度と寿命2,オーガナイズド・セッション)