二円筒試験におけるすずめっき熱拡散処理層の焼付き強さ : 二硫化モリプデンを添加したグリースの場合

概要

論文の詳細を見る
To clarify the seizure resistance of stainless steel rollers of which the surface layer was thermally diffused after being Sn-plated, a two-roller test was carried out with grease lubrication. From the tests, the following results were obtained. The coefficient of friction of the roller with the Sn-diffused layer at the incipient stage of seizure, when lubricated with grease containing molybdenum disulfide additive, was considerably higher than that without a diffused layer. The load at the incipient stage of seizure of the roller with the diffused layer was larger than that of the roller without the diffused layer, and the effect of the diffused layer on the increase in the seizure resistance of the roller was recognized. However, the seizure resistance of the roller was decreased due to the molybdenum disulfide additive. The critical temperature of the roller with the diffused layer was higher than 400℃, and this was higher than that without a diffused layer.
1996-09-25