残留応力場の表面疲労き裂伝ぱ挙動 : 疲労き裂伝ぱ則の検討と疲労き裂伝ぱ速度の評価

概要

論文の詳細を見る
Fatigue lives of plain carbon steel with residual stress were studied with special reference to the initiation and the propagation of surface cracks. Tensile residual stresses did not have influences on crack initiation lives, but increased the fatigue crack propagation rate for surface fatigue cracks. The propagation rate of a surface fatigue crack was controlled by the parameter of {(ΔK)^<0.5>(K_<max>)^<0.5>} in which ΔK and K_<max> were, respectively, the stress intensity factor range and stress intensity factor calculated from the maximum stress distribution containing residual stress measured at the stress cycles of the initiation of surface cracks. This parameter also served to help understand surface fatigue crack shape in a residual stress field. Finally, the equation of (ΔK)^p(K_<max>)^q≒K_<max>-p・K_<min> was derived under condition of both p+q=1 and minimum stress intensity factor |K_<min>|<K_<max>, which enabled us to discuss effects of K_<min> (<0) on fatigue crack propagation from the point of mechanical behavior of the plastically deformed layer left in the wake of the advancing crack.
社団法人日本機械学会の論文
1988-09-25