引張残留応力分布下の疲労き裂伝ぱ挙動 : 疲労き裂伝ぱ則とDugdaleモデルによる検討

概要

論文の詳細を見る
Fatigue crack propagation behavior in a tensile residual stress field has been experimentally examined, using plate specimens with residual stress distributed in a profile of thermal stress type. The fatigue crack growth law, using both range ΔK and maximum K_<max> of the stress intensity factor, has been obtained from fatigue tests under various tensile mean stresses in specimens without residual stress, and thereby changes of fatigue crack propagation rate due to tensile residual stress have been evaluated in terms of the value of K_<max> which can take into account initial residual stresses distributed along a crack, at relatively lower stress amplitudes. At higher stress amplitudes, however, the residual stress distribution in front of the crack tip has resulted also in changing the fatigue crack propagation rate in accordance with changes of plastic deformation at the crack tip, which has been discussed from a fatigue crack analysis based on the Dugdale model in which initial residual stresses can be taken into account in opening a fictitious crack governed by the surrounding elastic field.
社団法人日本機械学会の論文
1988-04-25