低温環境下における高引張綱溶接継手の疲労き裂伝ぱ挙動
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue crack growth rates in the base metal and the welds of HT80 steel welded joints were evaluated at temperatures ranging from room temperature down to 93 K. For the welds, the crack growth rates between room temperature and 174 K were dominated by residual stresses rather than temperatures. As the temperature decreased below 123 K, the crack growth rates of the base metal and the welds increased markedly because of cyclic cleavage during striation growth. The crack growth rates of the welds correlated with the effective stress intensity factor range, ΔK_<effR>, which was estimated by superposition of the respective stress intensity factors for the residual stress fields and for the applied stresses, when the crack growth was dominated by striation formation.
- 1987-08-25
著者
関連論文
- A533B圧力容器用鋼の高温水中における疲労き裂進展挙動に及ぼす熱時効の影響
- Ti-6Al-4V合金の疲労強度に及ぼすショットピーニングの影響
- Ti-6Al-4V合金の疲労き裂伝ぱ挙動に及ぼす異方性の影響(フラクトグラフィ特集)
- アルミ合金および軟鋼のストライエーション間隔の統計的検討 : 定量的疲労破壊事故解析へのフラクトグラフィの適用
- 破壊事故からの教訓と指標
- 失敗事例を活用した機械・構造物の損傷防止対策
- 赤外線応力測定における測定精度に及ぼす熱伝導の影響
- 赤外線法による応力集中係数および応力拡大係数範囲の決定
- 天井クレーン模擬プログラム荷重下の溶接補修材の疲労強度
- 応力集中係数および応力拡大係数の決定のための熱弾性効果の適用
- 天井クレーン模擬プログラム荷重下のガセット溶接継手の疲労強度
- 赤外線応力画像システムを用いた疲労き裂検出の試み
- 赤外線応力画像システムによる各種切欠き近傍の応力評価
- A533B鋼の機械的性質に及ぼす熱時効の影響
- 5. 材料力学 5・4 破損事例と材料力学 (機械工学年鑑)
- 材料力学
- 溶接部材および接合材の破損解析
- 変動荷重を受けるHT80鋼溶接継手の疲労き裂伝ぱ挙動の評価
- 溶接継手の疲労き裂伝ぱのフラクトグラフィ
- 溶接継手の疲労き裂伝ぱ挙動に及ぼす試験片寸法および予荷重履歴の影響
- 荷役機械部品の破損解析
- 低温環境下における高引張綱溶接継手の疲労き裂伝ぱ挙動
- 低温における構造用鋼の疲労き裂の延性-ぜい性遷移挙動
- 潜函工事用ボルトの疲労強度
- 低温におけるSM50A鋼溶接継手の疲労き裂伝ぱ挙動
- テルル快削鋼の疲れ強さ : 切削加工層と介在物が疲れ強さに及ぼす影響(第1報)