A533B鋼の機械的性質に及ぼす熱時効の影響
スポンサーリンク
概要
- 論文の詳細を見る
The influence of thermal aging on fracture properties, transition temperature of V-notch Charpy impact test, elastic-plastic fracture toughness, fatigue crack growth behavior and stress corrosion cracking of the base metal and welded joint of A533B steel were examined. The chemical compositions of the base metal and weld wire were adjusted, referring to those of reactor pressure vessels of old Japanese commercial nuclear power plants constructed before 1970. A step-cooling heat treatment was used as embrittling treatment. The transition temperature of the base metal and welded joint subjected to step-cooling rises approximately 30℃ due to the segregation of phosphorus. However, the step-cooling heat treatment has little influence on the fracture toughness, the crack growth behavior and stress corrosion cracking.
- 1993-09-25
著者
関連論文
- A533B圧力容器用鋼の高温水中における疲労き裂進展挙動に及ぼす熱時効の影響
- Ti-6Al-4V合金の疲労強度に及ぼすショットピーニングの影響
- Ti-6Al-4V合金の疲労き裂伝ぱ挙動に及ぼす異方性の影響(フラクトグラフィ特集)
- アルミ合金および軟鋼のストライエーション間隔の統計的検討 : 定量的疲労破壊事故解析へのフラクトグラフィの適用
- 破壊事故からの教訓と指標
- 失敗事例を活用した機械・構造物の損傷防止対策
- 赤外線応力測定における測定精度に及ぼす熱伝導の影響
- 赤外線法による応力集中係数および応力拡大係数範囲の決定
- 天井クレーン模擬プログラム荷重下の溶接補修材の疲労強度
- 応力集中係数および応力拡大係数の決定のための熱弾性効果の適用
- 天井クレーン模擬プログラム荷重下のガセット溶接継手の疲労強度
- 赤外線応力画像システムを用いた疲労き裂検出の試み
- 赤外線応力画像システムによる各種切欠き近傍の応力評価
- A533B鋼の機械的性質に及ぼす熱時効の影響
- 5. 材料力学 5・4 破損事例と材料力学 (機械工学年鑑)
- 材料力学
- 溶接部材および接合材の破損解析
- 変動荷重を受けるHT80鋼溶接継手の疲労き裂伝ぱ挙動の評価
- 溶接継手の疲労き裂伝ぱのフラクトグラフィ
- 溶接継手の疲労き裂伝ぱ挙動に及ぼす試験片寸法および予荷重履歴の影響
- 荷役機械部品の破損解析
- 低温環境下における高引張綱溶接継手の疲労き裂伝ぱ挙動
- 低温における構造用鋼の疲労き裂の延性-ぜい性遷移挙動
- 潜函工事用ボルトの疲労強度
- 低温におけるSM50A鋼溶接継手の疲労き裂伝ぱ挙動
- テルル快削鋼の疲れ強さ : 切削加工層と介在物が疲れ強さに及ぼす影響(第1報)