Hastelloy-Xの疲労/クリープ遷移挙動のその場観察

概要

論文の詳細を見る
Faligue creep transition in Hastelloy-X at elevated temperatures under tensile-tensile cyclic leading was studied by in-situ observation employing a SEM servo. The main results were as follows (1) Fatigue limit was not found at any temperature, since oxide-induced crack closure did not occur in vacuum. (2) In-situ observation showed that surface crack length increased at 700℃ and crack opening displacement increased at 800℃. Thus, fatigue crack initiated and propagated at 700℃, while, creep deformation accumulated at 800℃. (3) The fatigue life of specimens tested at 800℃ ere decreased under cyclic loading frequency from 30 Hz to 0.3 Hz. under these conditions, the fatigue at 800℃ was dominated by time dependent creep rupture. (4) Fatigue-creep transition occurred from 700℃ to 800℃. The mechanism of fracture at 700℃ was fatigue and that at 800℃ was creep deformation
一般社団法人日本機械学会の論文
1997-04-25