同一強度水準のADIの疲労信頼性に及ぼす凝固時の冷却速度の影響
スポンサーリンク
概要
- 論文の詳細を見る
The influence of cooling rate on the fatigue reliability of austempered ductile iron (ADI) was investigated with special attention given to a mesoscopic factor of fracture origin. The main results were as follows. (1) The fatigue strength of ADI could be improved by increasing the cooling rate. (2) Different kinds of casting defects were observed at the origin of fatigue crack in three types of ADI, which were produced through rapid, medium and slow cooling rates (designated as R, M and S materials, respectively). These are larger dross, spheroidal graphite and porosity in R, M and S materials, respectively. (3) The mesoscopic factors of fracture origin, which consisted of casting defects and matrix microstructure, could be quantitatively related to the fatigue life.
- 社団法人日本機械学会の論文
- 1996-03-25
著者
-
伊藤 吉保
いわき明星大学理工学部
-
伊藤 金彌
茨城大学大学院
-
鈴木 秀人
茨城大学工学部
-
西野 創一郎
茨城大学工大学院
-
? 偉民
茨城大学工学部
-
〓 偉民
茨城大学大学院
-
西野 創一郎
茨城大学工学部
-
伊藤 吉保
いわき明星大
関連論文
- 表面改質Mg合金鋳物の疲労強度に及ぼすスピネル皮膜のフラクタル性の影響
- 表面改質Mg合金鋳物の軽量化設計法の構築と安全性保証 : HAE陽極酸化処理を施したAZ91D材の疲労強度に及ぼす極硬質スピネル皮膜の影響(材料・構造の衝撃問題)
- 913 超硬質・自己潤滑コーティングを施したビスマス快削鋼の疲労破壊メカニズム解明
- 906 DLC 皮膜の表面特性に及ぼす基材硬度の影響
- 902 超硬質・自己潤滑コーティングを施した自動車部品用 Bi 快削鋼の摺動特性
- 121 自溶合金溶射部材の疲労特性に及ぼす再溶融処理加熱方法の影響(微視組織と疲労強度評価III, 疲労の実際と最新の話題 微視組織と疲労強度評価)
- 1004 異なる再溶融処理を施した Co 基自溶合金溶射材の疲労特性
- DLC表面改質によるAl製自動車摺動部品の高性能化デザイン
- 3D-CADを用いた工業用白金合金の疲労破壊解析
- 305 昆虫の翅グライダーに関する研究(学生賞セッションII)