ウィスカ強化アルミニウム合金の破壊解析
スポンサーリンク
概要
- 論文の詳細を見る
The fracture process of whisker-reinforced aluminum alloys is studied. First, tensile tests are carried out on specimens of various orientations. Dimple fracture occurs at the edge of the whisker fiber due to the stress concentration. It is also found that delamination occurs at the whisker matrix interface in the T-specimen. Then the fracture process is simulated by FEM. For the constitutive equation, Gurson's yield fuction is used. Void volume fraction is used as a fracture parameter and a conventional fracture analysis is carried out. Numerical results qualitatively agree with those of experiments. The delamination effect between the base metal and the whisker fiber is considered. It is concluded that the effect of the delamination is very small before fracture of the specimen.
- 一般社団法人日本機械学会の論文
- 1993-04-25
著者
-
菊池 正紀
東京理科大学理工学部機械工学科
-
平野 一美
機械技術研究所
-
平野 一美
機械技研
-
買買提明 艾尼
東京理科大学理工学部
-
菊池 正紀
東京理科大学工学部
-
買買提明 〓尼
中国新彊工学院機械工程系:(現)jsps外国人特別研究員
-
買買提明 艾尼
新彊工学院
-
菊池 正紀
東京理科大学 理工学部機械工学科
-
菊池 正紀
東京理科大学
関連論文
- 表面き裂の疲労き裂進展クライテリオンの検討 : 第1報,モードI負荷を受ける表面き裂のパリス則
- 1002 ベジエスプライン曲線を用いた3次元転位動力学法の開発(OS-10A マクロ・メゾ・マイクロ・ナノスケールを繋げるマルチスケール計算力学,OS-10 マクロ・メゾ・マイクロ・ナノスケールを繋げるマルチスケール計算力学)
- 1412 ジルコニウム中における刃状転位とC成分転位ループの相互作用の分子動力学法による解析(OS-14C 欠陥/析出物と相互作用,OS-14 電子・原子・マルチスケールシミュレーションに基づく材料特性評価)
- ジルコニウムの中性子照射の分子動力学法シミュレーション(OS13d 電子・原子シミュレーションに基づく材料特性評価)
- α鉄中の刃状転位の切り合いの計算機シミュレーション(OS13d 電子・原子シミュレーションに基づく材料特性評価)
- ニッケル基超合金中のγ析出物と超転位の相互作用の転位動力学シミュレーション
- 804 ニッケル基超合金における転位網を考慮したラフティングの計算機シミュレーション(OS08.電子・原子・マルチシミュレーションに基づく材料特性評価(1))
- 819 ジルコニウムの照射成長のキネティックモンテカルロシミュレーション(OS08.電子・原子・マルチシミュレーションに基づく材料特性評価(5))
- 257 Zr中の変位カスケードによる原子空孔集合体の構造変化の分子動力学シミュレーション(欠陥,OSO7 電子・原子・マルチシミュレーションに基づく材料特性評価)
- 2027 鉄中の銅析出物とらせん転位の相互作用の分子動力学シミュレーション(J01-1 材料や構造の破壊/損傷/マルチスケール解析(1),J01 材料や構造の破壊/損傷/マルチスケール解析)