Study on Coalescence Probability of Cracks Originating from Randomly Spaced Surface Defects and Associated Fatigue Life Distribution
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests were carried out on S50C steel specimens having four drilled holes with random circumferential distances in the critical section to investigate statistically the propagation behavior of surface cracks and their coalescence leading to a failure of the specimen. The important findings in the present study are summarized as follows: It was observed that the first crack coalescence occludes between adjacent holes with the minimum or second minimum distance. There was little difference between the number of cycles to crack coalescence and that to a failure. The distribution of the numbers of cycles to crack coalescence has been theoretically derived on the basis of crack coalescence probability assuming that the first crack coalescence occurs between adjacent two holes of the minimum distance or the second minimum distance. The theoretical distribution thus derived shows good agreement with the experimental result.
- 一般社団法人日本機械学会の論文
著者
-
TANAKA Tsuneshichi
Faculty of Engineering, Ritsumeikan University
-
OKADA Kenji
Takamatsu National College of Technol.
-
Sakai Tatsuro
Faculty Of Science And Engineering Ritsumeikan University
-
Okada Kenji
Takamatsu Technical College
関連論文
- Development of a Hydraulic Spring-Type, High-Speed Impact Fatigue Testing Machine and the Experimental Results
- Studies on Fatigue Damage Caused by Stresses below the E durance Limit : Probability Distributions of Crack Initiation Lives at Stresses near the Endurance Limit
- Effect of Loading Time on High-Cycle Range Impact Fatigue Strength and Impact Fatigue Crack Growth Rate
- The Propagation of the Fatigue Crack Crossing the Inrerrace of Metal Composites Under the Effect of Residual Thermal Stress
- On the Propagation Behavior of the Fatigue Crack along the Interface of Metal Composites
- Propagation of Fatigue Cracks in Parallel with the Interfaces of Metal Composites
- SB-10-3(017) Construction of Database on Heat Resistant Alloys and Some Analyses of Creep Properties(Creep Deformation and Fracture of Superalloys)
- A Probabilistic Study on Fatigue Life Distribution of a Metallic Material with Surface Defects Considering the Number of Initiated Cracks
- A Statistical Study on Fatigue Life Distribution Based on the Coalescence of Cracks from Surface Defects
- Effect of Heating and Cooling Speed and Hold Time on Thermal Fatigue
- ESTIMATION OF TENSILE STRENGTH DISTRIBUTION FOR CARBON FIBER WITH DIAMETER VARIATION ALONG FIBER
- Study on Crack Growth Behavior in Impact Fatigue : Part III, Fatigue Crack Growth Behaviors of 2017-T3 Aluminum Alloy
- Study on Crack Growth Behaviors in Impact Fatigue : Part II, Crack Clusure Behavior under Simple Impact Load
- Fatigue Crack Propagation Behaviors of Multilayered Low Carbon Steel-stainless Steel Composite Plates
- Study on Crack Growth Behavior in Impact Fatigue : Part 1,Impact Fatigue Crack Growth Characteristics of 0.1%C Aluminum Killed Steel
- Effect of Specimen Thickness on Fatigue Crack Propagation in High Strength Steels
- Effect of Aging Treatment on the Fatigue Crack Propagation of 18% Ni Maraging Steel
- Plane Bending Plastic Fatigue of Ni-Cr-Mo Steel
- Study on Coalescence Probability of Cracks Originating from Randomly Spaced Surface Defects and Associated Fatigue Life Distribution
- Effect of Loading Frequency on the Fatigue Strength of Steels at Elevated Temperatures
- Studies on Impact Fatigue : Part IV, Impact Fatigue Tests of 0.22%C Carbon Steel under -50℃ Low Temperature Atmosphere
- Notch Dependency of the Effect of Superimposed Stress of High Frequency on the Fatigue Strength
- Estimation of the Fatigue Life under Program Load Including the Stresses Lower than Endurance Limit
- Studies on Impact Fatigue : Part 1,Impact Fatigue Testing Machine and Impact Fatigue on Mild Steel
- Effect of Superimposed Stress of High Frequency on Fatigue Strength of Annealed Carbon Steel
- Studies on Impact Fatigue : part II, Inelastic Behavior of S50C Steel under Impact Fatigue Loads
- Fatigue Strength of 18% Ni Managing Steel and the Effect of Distributed Inclusions
- Studies on Impact Fatigue : Part V, Impact Fatigue Strength of 0.22%C Carbon Steel under-100℃ Low Temperature Atmosphere
- Effect of the Superimposed Stress of High Frequency on Fatigue Strength
- A Theoretical Study on Fatigue Life Distribution of Metallic Materials Based on the Distribution of Surface Defects