Development of a Hydraulic Spring-Type, High-Speed Impact Fatigue Testing Machine and the Experimental Results
スポンサーリンク
概要
- 論文の詳細を見る
In order to examine the threshold condition for the propagation of a through crack under the mixed mode, plane bending tests, cyclic torsion tests, and their various combinations are carried out under the condition of the stress ratio R=-1 using annealed center-cracked specimens made of carbon steel. Taking account of the frictional stress acting on the crack surface under cyclic torsion, and adopting the strain-energy density criterion, the threshold stress of crack propagation under the combination of plane bending and cyclic torsion can be deduced from the individual test results of plane bending and cyclic torsion.
- 一般社団法人日本機械学会の論文
- 1988-10-15
著者
-
Fujii Tsutomu
Tokyo Koki Seizosho Ltd.
-
TANAKA Tsuneshichi
Faculty of Engineering, Ritsumeikan University
-
NAKAYAMA Hideaki
Automobile Industry, Osaka Industrial University
-
MORI Tadao
Material and Components Group, Toshiba Corporation
-
KINOSHITA Ken-ichiroh
Faculty of Engineering, Ritsumeikan University
-
Nakayama H
Tottori Univ.
-
Nakayama H
Executive Office School Juridical Person Osaka Sangyo University
-
Kinoshita Ken-ichiroh
Kinoshita Metal Industry Co. Ltd.
-
Mori Tadao
Material And Components Group Toshiba Corporation
-
Tanaka T
Faculty Of Science And Engineering Ritsumeikan University
関連論文
- Effect of a Simulated Saturation Dive to 31 ATA on Pulmonary Function
- 14 Postural and Intentional Tremor during a Simulated Oxygen-helium Dive to 300m
- 11 Influence of Hyperbaric Heliox Environment (31 ATA and He-0_2) on Microvibration and Electroencephalogram
- Influence of Hyperbaric Heliox Environment at 31ATA on Microvibration and Electroencephalogram in Four Divers
- Power Spectral Analysis of Intentional and Postural Tremor During a Simulated Heliox Dive to 31ATA
- Development of a Hydraulic Spring-Type, High-Speed Impact Fatigue Testing Machine and the Experimental Results
- Studies on Fatigue Damage Caused by Stresses below the E durance Limit : Probability Distributions of Crack Initiation Lives at Stresses near the Endurance Limit
- Effect of Loading Time on High-Cycle Range Impact Fatigue Strength and Impact Fatigue Crack Growth Rate
- The Propagation of the Fatigue Crack Crossing the Inrerrace of Metal Composites Under the Effect of Residual Thermal Stress
- On the Propagation Behavior of the Fatigue Crack along the Interface of Metal Composites
- Propagation of Fatigue Cracks in Parallel with the Interfaces of Metal Composites
- EVALUATION OF WEIBULL PARAMETERS FOR STATIC STRENGTHS OF CERAMICS BY MONTE CARLO SIMULATION
- Relationship among Blood Lactate and Plasma Catecholamine Levels during Exercise in Acute Hypoxia
- Effect of Chronic Hypoxia on Oxidative Enzyme Activity in Rat Skeletal Muscle
- A Probabilistic Study on Fatigue Life Distribution of a Metallic Material with Surface Defects Considering the Number of Initiated Cracks
- A Statistical Study on Fatigue Life Distribution Based on the Coalescence of Cracks from Surface Defects
- Statistical Aspect of Fatigue Crack Propagation From Surface Defects
- Effect of Heating and Cooling Speed and Hold Time on Thermal Fatigue
- ESTIMATION OF TENSILE STRENGTH DISTRIBUTION FOR CARBON FIBER WITH DIAMETER VARIATION ALONG FIBER
- Study on Crack Growth Behavior in Impact Fatigue : Part III, Fatigue Crack Growth Behaviors of 2017-T3 Aluminum Alloy
- Study on Crack Growth Behaviors in Impact Fatigue : Part II, Crack Clusure Behavior under Simple Impact Load
- Fatigue Crack Propagation Behaviors of Multilayered Low Carbon Steel-stainless Steel Composite Plates
- Study on Crack Growth Behavior in Impact Fatigue : Part 1,Impact Fatigue Crack Growth Characteristics of 0.1%C Aluminum Killed Steel
- Effect of Specimen Thickness on Fatigue Crack Propagation in High Strength Steels
- Effect of Aging Treatment on the Fatigue Crack Propagation of 18% Ni Maraging Steel
- Plane Bending Plastic Fatigue of Ni-Cr-Mo Steel
- Study on Coalescence Probability of Cracks Originating from Randomly Spaced Surface Defects and Associated Fatigue Life Distribution
- Effect of Loading Frequency on the Fatigue Strength of Steels at Elevated Temperatures
- Studies on Impact Fatigue : Part IV, Impact Fatigue Tests of 0.22%C Carbon Steel under -50℃ Low Temperature Atmosphere
- Notch Dependency of the Effect of Superimposed Stress of High Frequency on the Fatigue Strength
- Estimation of the Fatigue Life under Program Load Including the Stresses Lower than Endurance Limit
- Studies on Impact Fatigue : Part 1,Impact Fatigue Testing Machine and Impact Fatigue on Mild Steel
- Effect of Superimposed Stress of High Frequency on Fatigue Strength of Annealed Carbon Steel
- Studies on Impact Fatigue : part II, Inelastic Behavior of S50C Steel under Impact Fatigue Loads
- Fatigue Strength of 18% Ni Managing Steel and the Effect of Distributed Inclusions
- Studies on Impact Fatigue : Part V, Impact Fatigue Strength of 0.22%C Carbon Steel under-100℃ Low Temperature Atmosphere
- Effect of the Superimposed Stress of High Frequency on Fatigue Strength
- A Theoretical Study on Fatigue Life Distribution of Metallic Materials Based on the Distribution of Surface Defects