Studies on Impact Fatigue : Part V, Impact Fatigue Strength of 0.22%C Carbon Steel under-100℃ Low Temperature Atmosphere
スポンサーリンク
概要
- 論文の詳細を見る
As a sequel of the impact fatigue investigation in 150 C low temperature atmosphere, a series of the fatigue tests in -100 C low temperature atmosphere were conducted. It was revealed that the impact fatigue strength became higher than the ordinary fatigue strength in the whole range of the stress cycles experimented, and this strength behavior can be interpreted such that the strain aging is hard to occur under both load conditions in such a low temperature atmosphere of -100 C, so that the fatigue strength is determined by the accumulation of the hysteresis energy only.
- 一般社団法人日本機械学会の論文
著者
-
TANAKA Tsuneshichi
Faculty of Engineering, Ritsumeikan University
-
Nakayama Hideaki
Faculty Of Engineering Yamanashi University
関連論文
- Second Harmonic Generation of Surface Acoustic Waves from a Dot Array : SAW and Communication Devices
- Development of a Hydraulic Spring-Type, High-Speed Impact Fatigue Testing Machine and the Experimental Results
- Studies on Fatigue Damage Caused by Stresses below the E durance Limit : Probability Distributions of Crack Initiation Lives at Stresses near the Endurance Limit
- Effect of Loading Time on High-Cycle Range Impact Fatigue Strength and Impact Fatigue Crack Growth Rate
- The Propagation of the Fatigue Crack Crossing the Inrerrace of Metal Composites Under the Effect of Residual Thermal Stress
- On the Propagation Behavior of the Fatigue Crack along the Interface of Metal Composites
- Propagation of Fatigue Cracks in Parallel with the Interfaces of Metal Composites
- A Probabilistic Study on Fatigue Life Distribution of a Metallic Material with Surface Defects Considering the Number of Initiated Cracks
- A Statistical Study on Fatigue Life Distribution Based on the Coalescence of Cracks from Surface Defects
- Effect of Heating and Cooling Speed and Hold Time on Thermal Fatigue
- ESTIMATION OF TENSILE STRENGTH DISTRIBUTION FOR CARBON FIBER WITH DIAMETER VARIATION ALONG FIBER
- Study on Crack Growth Behavior in Impact Fatigue : Part III, Fatigue Crack Growth Behaviors of 2017-T3 Aluminum Alloy
- Study on Crack Growth Behaviors in Impact Fatigue : Part II, Crack Clusure Behavior under Simple Impact Load
- Fatigue Crack Propagation Behaviors of Multilayered Low Carbon Steel-stainless Steel Composite Plates
- Effect of Endurance Training under Hypoxic Condition on Oxidative Enzyme Activity in Rat Skeletal Muscle
- Study on Crack Growth Behavior in Impact Fatigue : Part 1,Impact Fatigue Crack Growth Characteristics of 0.1%C Aluminum Killed Steel
- Effect of Specimen Thickness on Fatigue Crack Propagation in High Strength Steels
- Effect of Aging Treatment on the Fatigue Crack Propagation of 18% Ni Maraging Steel
- Plane Bending Plastic Fatigue of Ni-Cr-Mo Steel
- Study on Coalescence Probability of Cracks Originating from Randomly Spaced Surface Defects and Associated Fatigue Life Distribution
- Effect of Loading Frequency on the Fatigue Strength of Steels at Elevated Temperatures
- Studies on Impact Fatigue : Part IV, Impact Fatigue Tests of 0.22%C Carbon Steel under -50℃ Low Temperature Atmosphere
- Notch Dependency of the Effect of Superimposed Stress of High Frequency on the Fatigue Strength
- Estimation of the Fatigue Life under Program Load Including the Stresses Lower than Endurance Limit
- Studies on Impact Fatigue : Part 1,Impact Fatigue Testing Machine and Impact Fatigue on Mild Steel
- Studies on Impact Fatigue : Part III, Impact Fatigue Investigation on 99.5% Pure Aluminum and Duralumin
- Effect of Superimposed Stress of High Frequency on Fatigue Strength of Annealed Carbon Steel
- Studies on Impact Fatigue : part II, Inelastic Behavior of S50C Steel under Impact Fatigue Loads
- Fatigue Strength of 18% Ni Managing Steel and the Effect of Distributed Inclusions
- Studies on Impact Fatigue : Part V, Impact Fatigue Strength of 0.22%C Carbon Steel under-100℃ Low Temperature Atmosphere
- Effect of the Superimposed Stress of High Frequency on Fatigue Strength
- A Theoretical Study on Fatigue Life Distribution of Metallic Materials Based on the Distribution of Surface Defects