UNSTABLE TEARING FRACTURE OF SHEET SPECIMENS UNDER MODE II LOADING
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the J-integral resistance curve (J-R curve) and the instability fracture criterion of sheet specimens under Mode II loading condition, Mode II tests have been carried out on center cracked specimens of 2024-T3 aluminum ally. The dependence of the J_u-R curve (J-R curve for Mode II loading) on the specimen geometry is examined experimentally. Furthermore, the influence of the compliance of the loading system on the unstable fracture condition is studied experimentally, and the applicability of the tearing instability criterion proposed by Paris et al. to Mode II loading condition is investigated. It is shown that the influence of the specimen geometry on the J_u-R curve is relatively small. The unstable fracture point estimated by the tearing instability criterion is in good agreement with the experimental result, and it is shown that the tearing instability criterion is applicable to the Mode II loading condition.
- 一般社団法人日本機械学会の論文
著者
-
Ichikawa Masahiro
Department of Mechanical and Control Engineering, The University of Electro-Communications
-
Takamatsu Tohru
Department Of Mechanical And Control Engineering University Of Electro-communications
-
Ichikawa Masahiro
Department Of Mechanical And Control Engineering The University Of Electro-communications
-
Ichikawa Masahiro
Department Of Mechanical Engineering Ii University Of Electro-communications
関連論文
- Iatrogenic Drop Metastasis of Recurrent Meningioma in a Vascularized Free Omental Flap : Case Report
- Effects of Bias Voltage and Discharge Current on Mechanical Properties of TiN Film Deposited by DC Magnetron Sputtering
- Unification of Reliability and Confidence Level in Reliability-Based Design : The Case of 2-Parameter Weibull Distribution
- SUITABLE SAMPLE AREA AND NUMBER OF DIVISIONS IN THE ESTIMATION OF THE MAXIMUM CRACK LENGTH BY EXTREME VALUE ANALYSIS : Evaluation of Estimation Accuracy Independent of Distribution Forms
- Estimation of the Maximum Crack Length in Creep-Fatigue of SUS 316 L Based on Statistics of Extremes and Image Processing
- Measurement of Small Crack Lengths under Creep-Fatigue Condition by means of Image Processing
- Effect of Stress Gradient on the Stress Concentration due to Piled-up Dislocations
- A Statistical Consideration of S-N Tests (Specimen Allocation to the Inclined and Horizontal Parts of the S-N curve)
- Quantification of Subarachnoid Hemorrhage by Three-Dimensional Computed Tomography : Correlation Between Hematoma Volume and Symptomatic Vasospasm
- EXTREMELY SENSITIVE DEPENDENCE OF STRENGTH AFTER PROOF TESTING OF CERAMICS ON INITIAL STRENGTH
- A Statistical Study of Stress Corrosion Cracking Life by Separating Crack Initiation and Propagation Lives
- Mixed Mode Fracture Criterion in a Thin Sheet of 2024-T3 Al-Alloy : Solid-Mechanics, Strength of Materials
- UNSTABLE TEARING FRACTURE OF SHEET SPECIMENS UNDER MODE II LOADING
- Minimum Strength of Ceramics After Proof Testing : (The Case When Slow Crack Growth Occurs on Unloading)
- Elastic Solid with an Infinite Row of Collinear Cracks and the Fracture Criterion
- Combined Microsurgical and Endoscopic Removal of Extensive Suprasellar and Prepontine Epidermoid Tumors
- Temperature Dependence of Mode II Fracture Toughness
- Reliability-Based Consideration of ASME's Scatter Factor Used in Low-Cycle Fatigue Design Based on Geometrically Similar Model Tests
- Dependence of Distribution of Stress Corrosion Cracking Life of a High Strength Steel on Various Factors (Prediction Based on Statistical Natures of Crack Initiation and Propagation Lives and Its Experimental Examination)
- Radiation-Induced World Health Organization Grade II Meningiomas in Young Patients Following Prophylactic Cranial Irradiation for Acute Lymphoblastic Leukemia in Childhood : Three Case Reports
- Fracture Toughness Testing for Sheet Specimens under Mode II Loading
- Effects of Post Quenching on Mechanical Properties of TiN Film Coated on Steel Substrate
- Some Problems in Application of Three-Parameter Weibull Distributions toReliability Evaluation of Ceramics