Measurement of Small Crack Lengths under Creep-Fatigue Condition by means of Image Processing
スポンサーリンク
概要
- 論文の詳細を見る
In relation to the evaluation of remaining life of high-temperature components based on statistics of extremes, this paper is concerned with application of image processing to measurement of small crack lengths. Creep-fatigue tests were carried out on SUS 316 L. Smooth specimens were subjected to slow-fast cyclic strain of a total strain range of 1% at 65O℃ in air with ε^^.=2x1O^<-5>/s in tension and ε^^.=2x1O^<-3>/s in compression. Taking replicas of the specimen surface, the images of the replicas were put into the image processing unit. Using some new algorithms and conventional algorithms, individual crack lengths were measured. The crack length measured by means of image processing was compared with that determined by manual measurement with a microscope. The distribution of the small crack length was also studied. Furthermore, propagation and coalescence behavior of cracks was investigated by means of image processing.
- 一般社団法人日本機械学会の論文
- 1992-04-15
著者
-
TAKAMATSU Tohru
Department of Mechanical Systems Engineering, School of Engineering, University of Shiga Prefecture
-
Takamatsu Tohru
The University of Electro-Communications
-
Ichikawa Masahiro
Department of Mechanical and Control Engineering, The University of Electro-Communications
-
Matsumura T
Department Of Mechanical And Control Engineering University Of Electro-communications
-
Matsumura Takashi
NEC Corporation
-
Ichikawa M
Univ. Electro-communications Tokyo Jpn
-
Takamatsu T
Department Of Mechanical Systems Engineering School Of Engineering University Of Shiga Prefecture
-
Takamatsu Tohru
Department Of Mechanical And Control Engineering University Of Electro-communications
-
Ichikawa Masahiro
Department Of Mechanical And Control Engineering The University Of Electro-communications
-
Matsumura T
Gunma Univ. Gunma
関連論文
- Iatrogenic Drop Metastasis of Recurrent Meningioma in a Vascularized Free Omental Flap : Case Report
- Effects of Bias Voltage and Discharge Current on Mechanical Properties of TiN Film Deposited by DC Magnetron Sputtering
- Evaluation of the Fracture Toughness on the Surface Layer in HIP-Sintered Silicon Nitride
- Intra-Ball and Inter-Ball Variability of Ring Crack Initiation Load of Silicon Nitride Bearing Balls
- Ring Crack Initiation Load of Silicon Nitride Bearing Balls
- Unification of Reliability and Confidence Level in Reliability-Based Design : The Case of 2-Parameter Weibull Distribution
- SUITABLE SAMPLE AREA AND NUMBER OF DIVISIONS IN THE ESTIMATION OF THE MAXIMUM CRACK LENGTH BY EXTREME VALUE ANALYSIS : Evaluation of Estimation Accuracy Independent of Distribution Forms
- Estimation of the Maximum Crack Length in Creep-Fatigue of SUS 316 L Based on Statistics of Extremes and Image Processing
- Measurement of Small Crack Lengths under Creep-Fatigue Condition by means of Image Processing
- Effect of Stress Gradient on the Stress Concentration due to Piled-up Dislocations
- A Statistical Consideration of S-N Tests (Specimen Allocation to the Inclined and Horizontal Parts of the S-N curve)
- Evaluation of Fracture Strength of TiN Thin Film on Cemented Carbide
- Quantification of Subarachnoid Hemorrhage by Three-Dimensional Computed Tomography : Correlation Between Hematoma Volume and Symptomatic Vasospasm
- EXTREMELY SENSITIVE DEPENDENCE OF STRENGTH AFTER PROOF TESTING OF CERAMICS ON INITIAL STRENGTH
- A Statistical Study of Stress Corrosion Cracking Life by Separating Crack Initiation and Propagation Lives
- Mixed Mode Fracture Criterion in a Thin Sheet of 2024-T3 Al-Alloy : Solid-Mechanics, Strength of Materials
- UNSTABLE TEARING FRACTURE OF SHEET SPECIMENS UNDER MODE II LOADING
- Minimum Strength of Ceramics After Proof Testing : (The Case When Slow Crack Growth Occurs on Unloading)
- Elastic Solid with an Infinite Row of Collinear Cracks and the Fracture Criterion
- Combined Microsurgical and Endoscopic Removal of Extensive Suprasellar and Prepontine Epidermoid Tumors
- Temperature Dependence of Mode II Fracture Toughness
- COMPARATIVE STUDY OF FEULGEN DNA CYTOFLUOROMETRY OF HEART MUSCLE CELLS AND COLOUR IMAGE ANALYSIS OF TISSUE FIBROSIS : PROCEEDINGS OF THE 47th ANNUAL SCIENTIFIC MEETING OF THE JAPANESE CIRCULATION SOCIETY : Pathology Morphology
- Reliability-Based Consideration of ASME's Scatter Factor Used in Low-Cycle Fatigue Design Based on Geometrically Similar Model Tests
- Dependence of Distribution of Stress Corrosion Cracking Life of a High Strength Steel on Various Factors (Prediction Based on Statistical Natures of Crack Initiation and Propagation Lives and Its Experimental Examination)
- Radiation-Induced World Health Organization Grade II Meningiomas in Young Patients Following Prophylactic Cranial Irradiation for Acute Lymphoblastic Leukemia in Childhood : Three Case Reports
- Fracture Toughness Testing for Sheet Specimens under Mode II Loading
- Effects of Post Quenching on Mechanical Properties of TiN Film Coated on Steel Substrate
- Some Problems in Application of Three-Parameter Weibull Distributions toReliability Evaluation of Ceramics