3次元織物チラノ繊維強化SiC基複合材料の疲労挙動に及ぼす周波数の影響

概要

論文の詳細を見る
The tensile and fatigue tests of 3D-woven Tyranno fiber reinforced SiC matrix composites were conducted at room temperature. The tensile strength was not dependent on loading rate, but the strain at failure increases with a decrease in loading rate from 10 to 0.02MPa/s. The effect of frequency on fatigue behavior was studied between 20 and 0.02Hz with a sine wave form and a stress ratio of 0.1. It was shown that the fatigue failure was cyclic-dependent between 20 and 0.2Hz, but time-dependent between 0.2 and 0.02Hz. The reduction of Young's modulus and sliding stress of interface during fatigue was analyzed. The cyclic-dependent behavior was dominated by wear of interphase and damage on the surface of Si-Ti-C-O fiber during cyclic loading-unloading. The time-dependent behavior was controlled by stress corrosion cracking of fiber and matrix.
社団法人日本材料学会の論文
2002-12-15