エチレン-酢酸ビニル共重合体の動的弾性率における時間-温度-濃度等価性について

概要

論文の詳細を見る
The dynamic mechanical tests of samples of ethylene-vinyl acetate copolymers with various contents of vinyl acetate monomer (VAc) ranging from 0 to 25.3 wt % made at varying temperatures from 5℃ to 80℃ at frequencies ranging from 1 to 100 cycles/sec., and their dynamic tensile modulus E', E" were obtained. These were made the data for examining each sample with respect to its principle of superposition of time and temperature. It was found that the larger the melt index of the sample was the wider was the scatter of these data in it. The shift distance log a_T was larger than those given from WLF equation. The values of log a_<T2> computed from the following equation gave good straight lines on a plot of log a_<T2> vs. 1/T; log a_r=(1-φ)log a<T1>+φlog a_<t2> where log a_T and log a<T1> represent respective shift distance obtained from experiment and from WLF equation, and in present trial, φ was assumed to represent volume fraction of crystalline part of each sample. Time-concentration principle was also examined with a convenient assumption that one monomer composition in the copolymer act as a diluent or a low molecular plasticizer. It seemed that the principle of superposing time and concentration was formally applicable to the data of copolymer by regarding the content of one monomer composition as concentration.
社団法人日本材料学会の論文
1971-05-15