軟鋼の2段多重変動荷重疲労における低応力繰返しの効果
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue tests with two levels of cyclic stresses were conducted on mild steels (aluminum killed steels) . The higher stress levels were 1.20 and 1.42 times of the endurance limit and the lower ones were 0.80, 0.57 and 0.38 times. Two cycles of higher stresses and various cycles of lower ones in a loading period were repeatingly applied. Fatigue lives in terms of number of loading cycles, Z_f lineally decreased by log n_L, where n_L is the total number of lower stress cycles in a loading period. When the frequency of higher stress cycles was low, 1 Hz in the present study, the lives to failure also decreased compared with the ordinary frequency. It was concluded that the modified Miner's method was unable to be applied to these experimental results, because the values estimated by that method varied widely with n_L. Emphasis was placed on the need for a modified estimation method in which the rate of fatigue damage by lower stess cycles is not constant but decreases as increase of the lower cycles in a loading period.
- 社団法人日本材料学会の論文
- 1980-10-15
著者
関連論文
- 鋭敏化オーステナイト・ステンレス鋼の応力腐食割れ : 塑性誘起相変態の効果
- 215 材料特性検出のための磁化過程の応用 : バルクハウゼン効果雑音の応用(機械的性質)
- 高アルミナ室セラミックスの破壊面とアコースティックエミッション
- 319 セラミックスの破面とアコースティック・エミッション(セラミックス・ガラス)
- 136 疲労破壊におけるアコースティックエミッションの観測
- 炭素鋼の長寿命プログラム疲労に対する寿命の推定
- 疲労過程を考慮した場合の実働荷重疲労強度の推定
- 疲労過程を考慮した場合の実働荷重疲労強度の推定
- 電子顕微鏡による金属の疲労破面の観察
- 実働荷重下の金属の疲れ強さ : 実働応力波形による疲れ試験
- 透過ラウエ法によるアルミニウムの変形の研究
- 福井県における積雪深分布の一次近似
- 焼なまし純アルミニウムの疲労粒界き裂の生成
- 2-13 アルミニウム双結晶粒界付近の変形
- 107 疲労寿命への荷重繰返し速さの影響(疲労特性)
- 軟鋼の2段多重変動荷重疲労における低応力繰返しの効果
- アルミニウムの疲労き裂先端の塑性ひずみ分布
- (1-18) 純アルミニウムの粒界疲労き裂の生成
- 透過X線回折法による金属の疲労破壊に関する研究(I)
- 実働荷重における金属の疲れ破面