ダイヤモンドのHIP焼結(<特集>高圧力 : 固体の高圧物性, 反応, 実験技術)
スポンサーリンク
概要
- 論文の詳細を見る
Fine and coarse powders of diamond were mixed with Si and sealed in evacuated glass tubes to be HIP'ed at temperatures between 1300℃ and 1600℃ and at the pressure of 150MPa for 90min. The sintered materials were characterized by means of X-ray powder diffraction, microscope, SEM and EDS. Their densities and mechanical properties were measured. The sintering proceeded rapidly at temperature above 1400℃. The main reaction possibly takes place in the liquid state, because the melting temperature of Si is at 1410℃ in air. The X-ray diffraction patterns were indexed by diamond, Si and SiC. No trace of conversion from diamond to graphite was observed. Among the starting materials prepared, the highest strength was found in the sample whose mixing ratio of fine and coarse diamonds and Si was 1:3:1 in weight. An application of the products to high pressure anvils was attempted and the generation of 7.70GPa in 6-8 split-sphere type apparatus was confirmed.
- 社団法人日本材料学会の論文
- 1998-10-15
著者
関連論文
- Diamond/SiC アンビルを用いた高圧放射光X線実験の利用
- HIP合成した Diamond/SiC アンビルを用いた高温高圧発生III
- 704 Diamond/SiC複合体のHIP合成と超高圧アンビルへの応用(極限環境フォーラム)
- HIP生成ダイヤモンド/SiC複合体:熱的性質と高温高圧用アンビルへの実用化
- Diamond/SiC複合体のHIP合成と超高圧アンビルへの応用(極限環境)
- HIP合成ダイヤモンド/SiC複合焼結体の物性評価と高圧発生用アンビルへの応用
- 409 Diamond/SiC 複合体のHIP合成と超高圧アンビルへの応用(高圧力フォーラム, 複合材料の成形・加工最前線)
- ダイヤモンドのHIP焼結(高圧力 : 固体の高圧物性, 反応, 実験技術)
- Diamond-SiC 複合焼結体のHIP合成と高圧アンビルへの応用
- 408 Diamond-SiC複合焼結体のHIP合成と高圧アンビルとしての利用(「極限環境下での固体材料の合成と物性評価」,極限環境フォーラム)
- 103 HIP合成したダイヤモンド・SiC複合アンビルを用いた高温高圧X線実験(環境極限フォーラム 極限環境を利用した材料科学の最前線)
- Diamond-SiC複合体のHIP合成と高圧X線その場観察実験への応用