窒化けい素の2段繰返し変動荷重下における疲労き裂進展挙動

概要

論文の詳細を見る
In order to investigate the cyclic fatigue crack growth behavior of a gas-pressure-sintered silicon nitride under repeated two-step loadings, fatigue crack growth tests were carried out using compact type (CT) specimens. Crack length and macroscopic crack closure were measured using the unloading elastic compliance method. Regardless of repeated two-step loading patterns, the acceleration of fatigue crack growth rate was observed. High-level load execution was found to crash grain interlocking more severely and result in decrease of crack opening stress intensity factor, K_<op> under low-level loadings. The fatigue crack growth acceleration behavior under repeated two-step loadings, where maximum load was kept constant, could be explained by crack closure behavior measured by the macroscopic method. However, under repeated two-step loadings where minimum load was kept constant, macroscopic crack closure behavior could account for the acceleration behavior qualitatively but not quantitatively.
社団法人日本材料学会の論文
1997-12-15