高炉スラグを原料としたβ一Spodumene系結晶化ガラスの製造
スポンサーリンク
概要
- 論文の詳細を見る
Blast furnace slag containing CaO, MgO, Al_2O_3 and SiO_2 as major components was used as the raw material forβ-spodumene glass-ceramics. The batch compositions were modified by mixing blast furnace slag with SiO_2, Al_2O_3, Li_2CO_3 and nucleating agent TiO_2. The crystallization processes of the glasses based on the blast furnace slag were investigated using differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM) and electron diffraction (ED). It was found that the major crystalline phase was β-spodumene (Li_2O・Al_2O_3・4SiO_2) and the average thermal expansion coefficients between 25° and 700℃ were 40.1 and 47.2×10^<-7>℃^<-1> for two different samples.
- 社団法人日本セラミックス協会の論文
- 1990-07-01
著者
関連論文
- Na_2O-CaO-P_2O_5-SiO_2系ガラス中に晶出した(Na,Ca)(P,Si)O_3の構造の研究
- アルミナ-ジルコニア-グラファイト耐火物の性質に及ぼすプロセス・パラメーターの影響(第2報) : 焼成温度及び時間
- MgO-CaO-Al_2O_3-SiO_2-P_2O_5バイオガラス-セラミック系の結晶化に及ぼすAl/P比の影響
- カオリン-シリカ-アルミナセラミックスの気孔及び浸透構造
- アルミナ-ジルコニア-黒鉛(AZG)耐火物の性質に及ぼすプロセス・パラメーターの影響 (第1報) : 成形圧力及び焼成温度
- アンドレアゼンモデルにより設計された粒度分布をもつAl_2O_3-ZrO_2-黒鉛耐火物の性質
- CVD法によるβ-SiC及びSiC/TiCコンポジットの成長
- シリカガラスの結晶化に及ぼすジルコン添加効果 : 速度論的研究
- ブラスト ホニス スラグを原料粉末に用いたタイルの製造とその性質の研究
- CVD法により作製したβ-SiC膜の形態と赤外分光特性
- CaO添加剤によるLi_2O-Al_2O_3-SiO_2-TiO_2系ガラスの結晶化挙動
- CVD 法で合成した SiC の微細構造、テクスチャー及び相に及ぼすアルゴン添加の影響
- 高炉スラグを原料としたβ一Spodumene系結晶化ガラスの製造
- CaCN_2を添加したAIN超微粉末の焼結
- β-スポジューメン前駆体粉末の焼結に及ぼすLiF添加の効果
- MgO-CaO-Al_2O_3-SiO_2-P_2O_5系ガラスの結晶化に及ぼすCa/P比の影響