β-スポジューメン前駆体粉末の焼結に及ぼすLiF添加の効果

スポンサーリンク

概要

• 論文の詳細を見る

• The effect of LiF addition on the sintering of β-spodumene (Li_2O・Al_2O_3・4SiO_2, LAS) powders prepared by a sol-gel process was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) . Upon sintering LAS precusor powders pellet samples without LiF addition, obtained the crystalline phase was merely β-spodumene. The intensity of the (102), (211), (222) and (303) refections of the β-spodumene phase decreases with increasing LiF additive content up to 4.0 mass% and some β-spodumene converts to β-eucryplite. The activation energies for grain growth were 26.0 and 23.0 kcal/mol for the calcined LAS precursor powders with 1.0 and 3.0 mass% LiF (sintered at various temperatures for 10 h), respectively. The slopes of the linear dependence of the grain size on the cubic root of time are 0.35 and 0.37 for the LAS precursor powders with 3.0 mass% LiF sintered at 1250 and 1350℃, respectively, showing a diffusion controlled growth.

• 社団法人日本セラミックス協会の論文
• 2002-03-01

著者

• 王 木琴

  国立高雄応用科技大学機械工程系

• 呉 南均

  国立成功大学

• 呉 南均

  国立成功大学材料科学及工程学系

• 楊 〓

  国立成功大学材料科学及工程学系

• 温 紹炳

  国立成功大学資源工程学系

関連論文

• アルミナ-ジルコニア-グラファイト耐火物の性質に及ぼすプロセス・パラメーターの影響(第2報) : 焼成温度及び時間
• カオリン-シリカ-アルミナセラミックスの気孔及び浸透構造
• アルミナ-ジルコニア-黒鉛(AZG)耐火物の性質に及ぼすプロセス・パラメーターの影響 (第1報) : 成形圧力及び焼成温度
• アンドレアゼンモデルにより設計された粒度分布をもつAl_2O_3-ZrO_2-黒鉛耐火物の性質
• ブラスト ホニス スラグを原料粉末に用いたタイルの製造とその性質の研究
• CaO添加剤によるLi_2O-Al_2O_3-SiO_2-TiO_2系ガラスの結晶化挙動
• 高炉スラグを原料としたβ一Spodumene系結晶化ガラスの製造
• CaCN_2を添加したAIN超微粉末の焼結
• β-スポジューメン前駆体粉末の焼結に及ぼすLiF添加の効果

スポンサーリンク