24.8Li_2O・1.3MgO・73.9SiO_2ガラスの内部摩擦複合ピークの分離
スポンサーリンク
概要
- 論文の詳細を見る
Internal friction of 16.3NaO・33.7MgO・50.0SiO_2 and 24.8Li_2O・1.3MgO・73.9SiO_2 glasses was measured with an inverted torsion pendulum at frequencies below 1Hz. The gamma distribution function was the most appropriate for approximating the whole shape of the low- and high-temperature peak which appeared separately in the internal friction curve of 16.3Na_2O・33.7MgO・50.0SiO_2 glass among the tested distribution functions:lognormal, beta and gamma. The intermediate-and high-temperature peaks were separated from the composite peaks observed in the internal friction curves of 24.8Li_2O・1.3MgO・73.9SiO_2 glass by approximating those peaks with the gamma distribution function and the activation energies for those peaks were determined. The activation energies for oxygen and magnesium diffusion below the glass transition point in the 24.8Li_2O・1.3MgO・73.9SiO_2 glass were also determined by use of stable isotopes ^<18>O and ^<26>:Mg, respectively. Within experimental errors, the activation energies for the intermediate-and high-temperature peak agreed with those for oxygen and magnesium diffusion, respectively.
- 1995-11-01
著者
関連論文
- シェリュプスキー法によるガラスの均質度の高精度測定のための試料作製
- 陶磁器からの鉛溶出に及ぼす水蒸気雰囲気焼成の効果
- 物質工学実験における安全衛生向上の試み
- 水蒸気雰囲気焼成における釉からの鉛放出
- 水蒸気雰囲気における陶磁器の上絵付け焼成
- 24.8Li_2O・1.3MgO・73.9SiO_2ガラスの内部摩擦複合ピークの分離
- 電気伝導から見たK_2O-GeO_2系ガラスのゲルマン酸異常
- Na_2O・2SiO_2ガラスの溶出前期におけるアルカリ溶出速度とクラックの進行
- 16.3Na_2O・33.7MgO・50.0SiO_2ガラスの内部摩擦
- XNa_2O・(1-X)B_2O_3・2SiO_2ガラスの内部摩擦と酸素の拡散(第2報) : 酸素の拡散
- XNa_2O・(1-X)B_2O_3・2SiO_2ガラスの内部摩擦と酸素の拡散(第1報) : 内部摩擦
- 二ケイ酸リチウムガラス中の酸素の自己拡散係数 (無機材料の化学-1-)
- Na_2O-GeO_2系ガラスの分子動力学シミュレーション
- MXDORTOによる分子動力学シミュレーション結果のWebブラウザによる表示 - GUIを使った対話型簡易表示プログラム -