水蒸気雰囲気における陶磁器の上絵付け焼成
スポンサーリンク
概要
- 論文の詳細を見る
Amount of lead release from porcelain tableware, changes of the lead concentration distribution and the structure in the surface layer of the porcelain tableware during overglaze decoration firing in a water vapor atmosphere were investigated. Lead in the surface layer of the pocelain tableware was released by evaporation and surface exchange reaction between lead ions at the surface of the porcelain tableware and proton or hydronium ions in water vapor during firing in a water vapor atmosphere. Then the proton or hydronium ions introduced by the surface exchange reaction were released as water vapor formed by condensation reaction, and the silica-rich layer which contains α-quartz was formed at the surface. This silica-rich layer was found to act as a protection layer against lead release.
- 1997-03-01
著者
-
森田 直文
(株)ノリタケカンパニーリミテド
-
坂井 俊彦
新潟大学工学部
-
渡邊 隆
新潟大学工学部
-
滝沢 一貴
新潟大学工学部
-
坂井 俊彦
長岡工業高等専門学校
-
蟹江 隆
(株)ノリタケカンパニーリミテド
関連論文
- シェリュプスキー法によるガラスの均質度の高精度測定のための試料作製
- 陶磁器からの鉛溶出に及ぼす水蒸気雰囲気焼成の効果
- 物質工学実験における安全衛生向上の試み
- 水蒸気雰囲気焼成における釉からの鉛放出
- 水蒸気雰囲気における陶磁器の上絵付け焼成
- 24.8Li_2O・1.3MgO・73.9SiO_2ガラスの内部摩擦複合ピークの分離
- 電気伝導から見たK_2O-GeO_2系ガラスのゲルマン酸異常
- Na_2O・2SiO_2ガラスの溶出前期におけるアルカリ溶出速度とクラックの進行
- 16.3Na_2O・33.7MgO・50.0SiO_2ガラスの内部摩擦
- XNa_2O・(1-X)B_2O_3・2SiO_2ガラスの内部摩擦と酸素の拡散(第2報) : 酸素の拡散
- XNa_2O・(1-X)B_2O_3・2SiO_2ガラスの内部摩擦と酸素の拡散(第1報) : 内部摩擦
- 二ケイ酸リチウムガラス中の酸素の自己拡散係数 (無機材料の化学-1-)
- 陶磁器製造技術の変遷
- 洋食器製造の技術的進歩
- Na_2O-GeO_2系ガラスの分子動力学シミュレーション
- MXDORTOによる分子動力学シミュレーション結果のWebブラウザによる表示 - GUIを使った対話型簡易表示プログラム -