W/Oエマルションを反応場とする球状多孔質ジルコニア及びチタニア粒子の合成

概要

論文の詳細を見る
Spherical porous zirconia and titania particles were synthesized by the sol-gel process from zirconyl chloride, zirconium tetrapropoxide and titanium tetraisopropoxide in W/O emulsion, respectively. Zirconia particles are obtained by addition of urea and hexamethylenetetramine in a starting solution. When the molar ratio of zirconyl chloride, calcium chloride, urea, hexamethylenetetramine, N, N-dimethyl formamide and H_2O is 1:0.2:1.1:0.9:1.4:45, spherical porous zirconia particles could be synthesized. The particles occurred cubic and monoclinic form at 600℃, respectively. Peak pore-diameter of the particles was 4 nm. The pore volume increases with increase in calcium content. After the extraction of calcium by hot water, the specific surface area of the particles is enhanced 110 m^2/g. SiO_2-ZrO_2 binary particles are synthesized by using zirconium tetrapropoxide and 2-methoxyethanol. When the molar ratio of tetramethoxysilane(TMOS), zirconium tetrapropoxide, 2-methoxyethanol, H_2O and HCl is 0.7:0.3:5.25:20:3.6×10^<-4> the specific surface area of the particles was 260 m^2/g. After the extraction of SiO_2 parts by 1 M NaOH aqueous solution, the weight loss of the particle was 10 mass%. Titania particles are obtained by addition of diethanolamine or 2-methoxyethanol in starting solution. Peak pore-diameter of the particles is 4 nm when the molar ratio of diethanolamine to titanium tetraisopropoxide was 1.5. By calcination at 500 and 700℃, the particle occurred anatase and rutile type, respectively. TiO_2-SiO_2 binary particles are synthesized by using 2-methoxyethanol. When the molar ratio of titanium tetraisopropoxide, TMOS, 2-methoxyethanol, H_2O and HCl is 0.4:0.6:4:20:1.8×10^<-3> the specific surface area of the particles was 180 m^2/g after the extraction of SiO_2 parts by 0.1 M NaOH aqueous solution.
社団法人日本セラミックス協会の論文
1998-12-01

W/Oエマルションを反応場とする球状多孔質ジルコニア及びチタニア粒子の合成

スポンサーリンク

概要

著者

関連論文

スポンサーリンク