超急冷法で調製したLi_2O-K_2O-Al_2O_3-SiO_2-F系ガラスの結晶化
スポンサーリンク
概要
- 論文の詳細を見る
The crystallization process of the rapidly quenched glasses in the system Li_2O-K_2O-Al_2O_3-SiO_2-F has been investigated. Batches of the lepidolite composition were melted at 1773 K for 10 minutes and quenched with a twin roller apparatus. Lepidolite and β-eucryptite were precipitated at 773 K and 873 K, respectively. However, it was requisited to keep the glass at 773 K for more than 1 hour for the precipitation of lepidolite. The thermal conductivity of the glass-ceramics heated at 773 K for 1 hour and then at 973 K for 2 hours was larger than fluorphrogopite glass-eramics, and its thermal expansion coefficient and dielectric properties were similar to those of fluorphrogopite glass-ceramics.
- 社団法人日本セラミックス協会の論文
- 1990-06-01
著者
関連論文
- WCの放出CKX線スペクトルの結晶性および観測角度依存性
- 機械的合金化したTi-hBN粉末中のBの状態分析
- メカニカルアロイング処理によるTiC生成反応のEPMA状態分析
- メカニカルアロイング法によるNb_3Al複合材の作製
- 高分解能蛍光X線分光法を用いた浅間火山岩中のFeの化学状態分析
- 希ガスイオン照射したC60のX線分光解析
- 2J01 PLD で作製したアモルファス In-Zn-O 透明導電膜
- ファンダメンタルパラメーター法によるスラグ,岩石の蛍光X線分析
- 乾式摩砕法によるカオリンからのムライトの合成
- ミリングによる黒鉛の構造変化
- いぶし瓦表面の汚染
- C K-emission Band Spectra of Carbons and Related Substances
- X線OK, BK放出スペクトルによるPbO, B_2O_3,SiO_2および熔融混合物のマイクロプローブ状態解析
- いぶし瓦のサビの生成のおよぼす鉄化合物と燻化条件の影響
- いぶし瓦の表面状態におよぼす燻化条件の影響
- 土練押し出し成形機による成形性に関与する粘土の可塑性の評価
- イオンビームスパッタリングにより作製したMgO膜の構造
- 超急冷法で調製したLi_2O-K_2O-Al_2O_3-SiO_2-F系ガラスの結晶化
- いぶし瓦表面炭素の微細構造
- c-BN膜の生成に及ぼす自己バイアス電圧の影響
- イオンプレーティング法で作製したBN膜の大気中での変質
- リシア雲母組成ガラスの結晶化に及ぼすジルコニアの影響
- 第55回日本セラミックス協会功績賞を受賞して 陶磁器原料資源の利用技術開発
- メカニカルアロイング法によるNbB2分散Al3Nb複合材の作製
- メカニカルアロイング法によるNbC分散Al3Nb複合材の作製
- C K-emission Band Spectra of Carbons and Related Substances
- T′型214相超伝導体における希土類置換効果 (酸化物超伝導体の材料プロセス化と特性評価)
- けい光X線による浮遊じんあい中の亜鉛および鉛の分析
- 無限層Sr1-xLaxCuO2の高圧合成と超伝導性 (酸化物超伝導体の材料プロセス化と特性評価)