ケイ酸ナトリウム-アルミン酸ナトリウム系沈殿反応による硬水中のカルシウムイオンの捕捉

概要

論文の詳細を見る
As to builder effect in synthetic detergent, the gelatinous precipitate was prepared by adding mixed solutions (Al/(Al+Si) molar ratio 0.17-0.83 of sodium silicate and sodium aluminate into hard waters (0.6×10^<-3>-12. 0×10^<-3>Ca^<2+> mol dm^<-3>). The capturing and its mechanism of calcium ion in suspension (pH7-11) of the gelatinous precipitate were investigated as against synthetic A-type zeolite (Na_2(Al_2Si_2O_8)・4. 5H_2O) used as a common builder. Characteristics of the gelatinous precipitate after capturing calcium ion were determined by X-ray diffraction, infrared spectroscopy, chemical analysis, dissolution test, measurements of specific surface area and ion-exchange capacity. The capturing capacity of calcium ion in suspension (pH 10-11) after adding the mixed solutions into hard water of 12.0×10^<-3> Ca^<2+> + mol dm^3 increased remarkably against those of individual solutions. In a mixed solution having Al/ (Al+Si) molar ratio of 0.5, the calcium ion in hard water was captured up to 95% in a shorter time as against the synthetic A-type zeolite. The composition of gelatinous precipitate after capturing calcium ion was formulated as Ca(Al_<1.4>Si_<1.7>O_<605>)・5.2H_2O. Also results of infrared spectrum and dissolution of calcium ion in water of the gelatinous precipitate showed that most of the calcium ion was strongly captured to the precipitate. Moreover most of the captured calcium ion as about 70% was exchangeable with sodium ion. That is, in the earlier stage of the reaction after adding mixed solution into hard water, a low crystalline precursor as familiar synthetic A-type zeolite was formed and changed finally to a low crystalline precursor like zeolite (gismoudine) indicating as Ca(Al_2Si_2O_8) 4H2_O by ion exchanging of Na^+ →Ca^<2+>.
社団法人日本セラミックス協会の論文
1990-11-01

ケイ酸ナトリウム-アルミン酸ナトリウム系沈殿反応による硬水中のカルシウムイオンの捕捉

スポンサーリンク

概要

著者

関連論文

スポンサーリンク