In order to study the viscoelastic behaviour of high polymers, an apparatus is required which enables the measurement of dynamic modulus and loss factor in a wide range of frequency and temperature. An apparatus was constructed for this purpose, which covers a range from 0.01 cps to 20 cps of frequency, from 20℃ to 160℃ of temperature, and from about 10^7 to 10^<11> dynes/cm^2 in the value of dynamic Young's modulus. The forced vibration of specimen was used in stead of resonant vibration, because the measurement could be carried out at any desirable frequency. The dynamic Young's modulus E' and loss factor tan δ can be obtained from the amplitude ratio and phase difference between stress and strain in the specimen, which is subjected to longitudinal vibration. In practice, the displacement of one end of the film-shaped specimen was detected by a wire strain gauge which was fixed to the driving clamp of specimen. The force was similarly detected by another strain gauge which was fixed to the other clamp, having much higher stiffness as compared to the stiffness of specimen. The electrical outputs from two strain gauges, which are proportional to the displacement and force respectively, are amplified and lead to the horizontal and vertical axes of afterglow cathode-ray oscillograph. From the Lissajous' figure thus obtained the elastic modulus E' and loss factor tan δ can be easily calculated. The two amplifiers were constructed identically, so that the electrical phase lag and temperature variation of sensitivity cancelled each other. When the frequency is higher, both electrical outputs are led into a specially devised circuit by which the values of E' and tan δ can be measured directly from the reading of the dial in potentiometer and of voltmeter. The observation of the Lissajous' figure in cathod-ray tube was also useful for watching the state of movement and the distribution of tension in the specimen. The specimen was surrounded by a cylindrical metal tube and heater element and the temperature of the atmosphere around specimen was controlled in the accuracy of 0.1℃ by a saturable core reactor system. The dynamic Young's modulus and loss factor of polyvinylacetate-styrene graft copolymers (29% and 37% styrene) have been measured over the temperature range of glass transition. Master curves for these specimens could be obtained following the ordinary reduced variable method.
- 社団法人日本材料学会の論文
- 1961-05-15
著者
関連論文
- 粘稠物質のロール面上の縞模様III(高分子)
- 可塑性物質の非線形粘弾性現象 : 分散系のレオロジー,その他
- 6p-A-5 可塑性物質の非線型粘弾性
- バターのチクソトロピーと結晶化度 : レオロジー一般
- 粘稠物質のロール面での縞模様 (II) : 高分子
- 粘稠物質のロール面での異常流動 : 高分子
- 練圧によるバターの粘度の変化 : レオロジー一般
- 負性容量回路を用いた圧電体の弾性率制御
- Q&Aコーナー
- 圧電高分子膜パネルの遮音制御について
- 213 圧電性高分子フィルムによる遮音・吸音
- 206 負性容量回路を結合した圧電材料の遮音および防振性能について(音のダンピング設計3)
- 負性容量回路を結合した圧電材料における遮音性能および防振性能の任意制御
- 204 負性容量回路を結合した圧電材料の遮音および防振性能について(一般 : 制振)
- 負性容量回路を結合した圧電フィルムの遮音性能について
- 負性容量回路を結合した圧電材料の遮音および防振性能について(その2)
- 負性容量回路を結合した圧電材料の遮音および防振性能について
- 1p-L-11 Poly-γ-benzyl-L-glutamateの側鎖による圧電緩和
- 酢酸セルロースの複素圧電率の温度による分散吸収
- 1p-K-6 ポリメチルグルタメートの圧電効果
- 7a-K-10 高分子の複素圧電率の温度変化
- 5p-M-9 不均貭高分子の粘彈性の梯子模型
- 5p-M-8 ポリ塩化ビニル・スチレン・グラフトポリマーの動的粘弾性
- PE. MMAグラフト重合体の動的粘弾性 : 高分子
- 6p-A-4 自動記録式粘彈性計の試作
- 3078 座の機構に関する実験的研究(第2報) : 座の動的変形測定装置としての多次元図形シンクロスコープの試作(計画)
- 負性容量回路を用いた圧電体の弾性率制御
- 12a-D-3 コラーゲン溶液の動的粘弾性
- ミルクおよびミルクゲルのレオロジー : 分散系のレオロジー : レオロジー特集号
- 平行板プラストメーターによる可塑性脂肪の粘弾性 : 分散型のレオロジー
- 平行板プラストメーターによる粘弾性の研究 : 高分子
- 外部電気回路導入による圧電性高分子の粘弾性変化に寄与するパラメータの検討
- 被照射シリコンオイルの放線応力,粘土,動的粘弾性 : 高分子のレオロジー
- 電磁変換式粘弾性測定器の試作 : レオロジー一般
- 振動板粘度計の改良について : レオメーター
- 架橋ポリエチレンの粘弾性 : 高分子レオロジー
- 13p-D-13 ポリ塩化ビニル・アクリロニトリル・グラフト共重合体の粘彈性
- グラフト重合物の粘弾性 : PMMA-PVAについて : 高分子
- 直読式固体粘弾性測定器の試作 : レオロジー一般
- ポリ醋酸ビニルの粘弾性スペクトル : 高分子
- 直讀式固体粘弾性測定器の試作 : 高分子
- コラーゲンのレオロジー
- 高分子物性の最近の研究
- 最近の粘弾性測定装置