傍熱型受信管のヒータ断熱について
スポンサーリンク
概要
- 論文の詳細を見る
This study was made to reveal some causes of break-down of the folded heater and thus to establish more effective way of preventing the break-down of heater wire. The broken parts of heater wire were brittle, and our microscopic observations found that the brittle parts showed large spheroidal crystal grains, whereas the unbroken part showed grains similar to fiber structure. Treatments of heater wire by three different methods, (e.g., wet hydrogen annealing, dry hydrogen annealing and oxygenate annealing treatments), before coating of the insulating pastes over its surface, showed that the oxygenate annealing treatment was most effective to prevent the break-down of heater wire under our experimental conditions. The reason seems ot be that the oxygenate annealing treatments etch off the metallographically instable surface of heater wire caused by the graphite lubricants and other impurities enfolded during the drawing process of wire, and serve to prevent coarsing of the crystal grains. The heater insulating pastes containing some nitrocelluloses which are added as the binder are inferior to the pastes containing 9 aqueous aluminium nitrates for the purpose to prevent the break-down of heater wire. Considering the facts that the above mentioned instable surfaces which cause the break-down of heater wire certainly are not removed sufficiently in the case of nitrocellulose pastes, we can understand the difference between the nitrocellulose pastes and the aluminium nitrate pastes for the prevention of the break-down of heater wire. The break-dwon of heater wire was prevented very effectively using the tungsten wire doped with 0.2% of thoria. The cause of break-dwon of bent part of heater results from the fact that the insulating coating of the bent part is scraped off by the sleeve during long operation and as a result the short circuit accident is induced. The short circuit accidents may be prevented by lessening the size of fault spot which is subjected to scrapping during the bending process. It seems that the size of fault spot has some relations to binder contained in insulating pastes and the shape of forming brade of the heater folding machine.
- 社団法人日本材料学会の論文
- 1959-02-15
著者
関連論文
- 小型電子管ガラス外囲器の熱衝撃試験に関する研究
- Fe-Ni-Cr系合金426の酸化の研究
- ガラスと金属の封着の機構
- ガラス-鉄封止について
- コバールの酸化被膜に関する研究
- 小型真空管のガラス部分の強さと,それに用いるガラスの熱膨張係数との関係について
- 傍熱型受信管のヒータ断熱について
- 受信管陰極用炭酸塩粒子について
- 結晶径を異にし同じ誘電率を示すBaTiO_3磁器の電気的特性について
- 圧縮応力を持つハーメチックシール中の応力分布
- ガラス対金属封止における接着機構
- ハーメチックシール
- 磁器化BaTiO_3の再焼結温度および粒度と物理定数との関係
- ガラスと金属の接着機構 (II)
- ガラスと金属の接着機構 (I)
- 小型電子管ガラス外囲器の熱衝撃によるクラックについて
- セレン半導体の電気的性質について