磁器化BaTiO_3の再焼結温度および粒度と物理定数との関係
スポンサーリンク
概要
- 論文の詳細を見る
It is well known that the properties of ceramic capacitors are greatly affected by particle size, composition forming pressure, impurity and firing temperature. Though there have been many reports made concerning these factors, but little is not known of the method to recover the BaTiO_3 once vitrified, and of the effect of using such materials on the propertis of BaTiO_3. This experiment was carried out to reveal the effect of such materials on the properties of the capacitor. In this experiment was carried out to reveal the effect of such materials on the properties if the capacitor. In this experiment, the crushed and classified powder of BaTiO_3 once vitrified were used as raw materials. The classified powder (100-150 mesh, 150-200 mesh, 200-270 mesh, 270-400 mesh,) pressed 17.5mmφ. 1.2mm thick were fired at various temperatures. The dielectric constant, the dielectric loss, the change of lattice constant, the water absorption, the shrinkage and the curie point were respectively measured. The results obtaind are summarized as follows : 1. The dielectric constant, the dielectric loss and the shrinkage increased with increased temperature. 2. The water absorption decreased with increased temperature. 3. The curie point was lowerd with increased temperature. 4. The lattice was expanded with increased temperature. 5. The effect on the bubbles of the classified particles growing large was equal to the rise of the firing temperature. 6. The porosity of the specimens calculated from the dimension and that calculated from the dielectric constant did not agree with each other.
- 社団法人日本材料学会の論文
- 1964-10-15
著者
関連論文
- ガラスと金属の封着の機構
- ガラス-鉄封止について
- コバールの酸化被膜に関する研究
- 小型真空管のガラス部分の強さと,それに用いるガラスの熱膨張係数との関係について
- 傍熱型受信管のヒータ断熱について
- 結晶径を異にし同じ誘電率を示すBaTiO_3磁器の電気的特性について
- ハーメチックシール
- 磁器化BaTiO_3の再焼結温度および粒度と物理定数との関係
- ガラスと金属の接着機構 (II)
- ガラスと金属の接着機構 (I)