EVALUATION OF FATIGUE STRENGTHS OF WC CERMET- AND 13Cr STEEL-SPRAYED MATERIALS
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests have been conducted at a room temperature in laboratory air using specimens of medium carbon steel(S45C), low alloy steel (SCM435) and titanium alloy (Ti-6Al-4V) with high velocity oxy-fuel(HVOF) sprayed coating of a cermet(WC-12%Co) and S45C with wire flame spraying(WFS) sprayed coating of a 13Cr steel(SUS420J2), and the fatigue strength and fracture mechanisms were studied. The fatigue strength evaluated by nominal stress was strongly influenced by substrate materials and the thickness of sprayed coatings.Detailed observation of crack initiation on the coating surface and fractuer surface revealed that in the WC cermet-sprayed materials, small defects initiated at WC grain boundaries coalesced and then the crack grew rapidly in the coating, while in the 13Cr steel-sprayed material, many microcracks were initiated from defects on the coating and coalesced to be a main crack. Cracks were initiated in the substrate due to the stress concentration of the crack in the coating, which was modeled by finite element analysis. The fatigue strength of the sprayed materials was dominated by that of the sprayed coating. Thus, the fatigue strength could be evaluated uniquely in terms of the true stress on the coating surface.
- 社団法人日本材料学会の論文
- 1998-03-15
著者
-
Ogawa Takeshi
Graduate School Of Life And Environmental Sciences Osaka Prefecture University
-
Harada Yoshio
TOCALO Co.
-
Ogawa Takeshi
Dept. of Internal Med., Inst. of Clin Med, univ. of Tsukuba
-
Harada Yoshio
Tocalo Co. Ltd.
-
Tokaji Keiro
Dept. of Mechanical and Systems Engineering, Gifu Univ.
-
Tokaji K
Dept.of Mech.eng. Gifu University
-
Tokaji Keiro
Dept. Of Mechanical And Systems Engineering Gifu Univ.
-
Ejima Toshikatsu
Dept.of Mech.Eng., Gifu University
-
Kobayashi Yoshifumi
Tocalo Co., Ltd.
-
Kobayashi Yoshifumi
Research Laboratory Tokico Ltd.
-
Ejima Toshikatsu
Dept.of Mech.eng. Gifu University
-
OGAWA Takeshi
Department of Pure and Applied Sciences, University of Tokyo
-
OGAWA Takeshi
Department of Pure and Applied Sciences University of Tokyo
-
HARADA Yoshio
TOCALO Co., Ltd.
関連論文
- SB-12-5(119) Collaborative Research on Themo-Mechanical and Isothermal Low-Cycle Fatigue Strength of Ni-Base Superalloys and the Protective Coatings at Elevated Temperatures in Japan.(Thermo-Mechanical Fatigue of Superalloys & Coatings)
- -30-THE EFFECT OF PHYSICAL TRAINING ON THE AUTONOMIC NERVOUS FUNCTION AND ITS ROLES IN IMPROVING THE EXERCISE TOLERANCE IN PATIENTS WITH OLD MYOCARDIAL INFARCTION
- Undesirable Effect of Local Cellular Transformation in Microstructurally-Controlled Ni-base Superalloys Subjected to Previous Damage on High Temperature Fatigue Strength and the Prevention : For Recoating and Refurbishment Technology
- Corrosion Behavior of Thermally Sprayed WC Coating in Na_2SO_4 Aqueous Solution
- Electrochemical Characteristic of WC Thermal Spray Materials in Na_2SO_4 Solution(Student Poster Session)
- Corrosion Behavior of WC Thermal Spray Coatings in Na_2SO_4 Solution
- OS9(5)-21(OS09W0305) Sensitive Strain Monitoring of SiC Fiber/Epoxy Composite Using Electrical Resistance Change
- Fatigue Crack Initiation and Early Growth Behavior of a Ferritic Stainless Steel in Laboratory Air and in 3%NaCl Aqueous Solution
- OS11(5)-21(OS11W0016) Effect of Ferritic-Austenitic Phase Fraction on Corrosion Fatigue Behavior in Stainless Steels
- OS10(1)-4(OS10W0154) Mechanical Properties of Lead-Free Solders Predicted by Indentation Testing
- THE MECHANISMS OF STRESS-INDUCED ST SEGMENT ELEVATION AND NORMALIZATION OF NEGATIVE T WAVES IN PATIENTS WITH PREVIOUS MYOCARDIAL INFARCTION : Ischemic Heart Disease (III) : III : 48 Annual Scientific Meeting, Japanese Circulation Society
- Mechanism of corrosion resistance degradation of Cr-plated parts due to heat treatment and its prevention
- X-Ray Evaluation of Pulse-Plated Crack-Free Cr Layer(Materials Evaluation by X-ray and Neutron Diffractions)
- EVALUATION OF FATIGUE STRENGTHS OF WC CERMET- AND 13Cr STEEL-SPRAYED MATERIALS
- FATIGUE STRENGTH AND FRACTURE MECHANISMS OF WC CERMET-SPRAYED STEEL
- Zeros of Partition Function and High Temperature Expansion for the Two-Dimensional Ising Models : Condensed Matter and Statistical Physics
- Critical Compressibility Factor of Two-Dimensional Lattice Gas : Kagome and Diced Lattices : Condensed Matter and Statistical Physics
- STATISTICAL DISTRIBUTION PATTERNS IN MECHANICAL AND FATIGUE PROPERTIES OF METALLIC MATERIALS
- A Study on Interspecific Hybrids and Selfed Progeny of Lycoris by Means of Fluorescence in situ Hybridization
- O-07. Speciation of Lycoris analyzed by in situ hybridization and DAPI banding(Abstracts of the oral and poster presentations,Abstracts of the 55th Annual Meeting of the Society of Chromosome Research)
- Micropropagation using Leaf Blades in Genus Lycoris
- Genome Differentiation in Lycoris Species (Amaryllidaceae) Identified by Genomic in situ Hybridization
- Genetic Segregation of Allozymes in Selfed Progenies of Diploid Lycoris Species (Amaryllidaceae)
- Thermal Diffusivity Measurement for Thermal Spray Coating Attached to Substrate Using Laser Flash Method