炭素鑄鋼中に於ける不純物としての錫の二三の影響に就て

概要

論文の詳細を見る
The authors described the experiments on the effects of increasing the tin content in a cast plain carbon steel containing 0.30% carbon. A complete investigation was not attempted, but the influence of the element on some of the useful properties of the steel was examined. The steels used were 29 steels containing up to 1.0% tin. They were taken from liquid steel made with a 20 ton basic open hearth furnace. It was found that tin has practically no effect on the A_1 point, but progressively raise the A_3 temperature of steel. In the steels containing up to 0.6∿0.8% tin, tin has practically no effect on the tensile strength, while with higher amounts somewhat decreases the maximum stress. Even the smallest amount, however, lowers the shock resisting properties of these steels, and if the tin content exceeds 0.2% the effect is serious. This effect is much more detrimental if the steels are tempered at a low temperature, or if they are allowed to cool slowly after tempering. The ill-effect of tin on the impact strength of these steels may be minimized by quenching after a full tempering. The influence of tin on case hardening process has been examined and as a result, it may be stated that the presence of tin injurcs the diffusion of carburizing. As for corrosion resistance, tin bearing steels are more resistant to atmospheric and some acid attack.
社団法人日本鉄鋼協会の論文
1942-07-25