鑄鐵の腐蝕現象(第三報) : 鑄鐵の腐蝕機構に關する諸實驗
スポンサーリンク
概要
- 論文の詳細を見る
In the previous reports the corrosion tests of many kinds of cast iron having various compositions and structures were carried out, and determined that the corrosion amount in a dilute nitric acid solution (0.5 N) is very small with the gray cast irons these contain free ferrite or greater amount of sulphide in pearlite matrix, this kind of gray cast iron evolves a pretty amount of gas in such a dilute nitric acid while the gray cast irons of pearlite matrix do not evolve any gas in the nitric acid solution of the same concentration. Then the rate of evolution of gas was measured and the chemical composition of the gases were determined. The gases evolve always periodically and greater part of them are hydrogen. From this fact and other experimental results, the writer concluded as following. In a dilute nitric acid gray cast iron first evolves hydrogen as a result of the electrolytic action caused by graphite (Cathode) and ferrite (Anode) while the ferrite is anodically oxidized and temporarilly brought to passive state, so that the dissolution ceases. In the next stage the passive state is destroyed by the acid and direct reaction between iron and nitric acid takes place, in this stage ferrite is severely attacked but non gas is evolved and instead of hydrogen ammonia and hydroxylamine these are soluble in the solution or complex iron salt are formed. In the 3rd stage hydrogen is evolved again by electrolytic action as the former case. These changes are repeated periodically in the progress of dissolution of gray cast iron in a dilute nitric acid. In another experiment the electrode potentials of various structural constituents of gray cast iron were measured in a normal ferrous chloride solution against the normal calomel electrode at 30℃. The results are as following ; graphite cathodically treated in 1N hydrochloric +0.2750^u, Fe_aC -0.2357^u, Fe_3P -0.2971^u, MnS 0^u, FeS -0.3600^u, [60% MnS+40% FeS] (solid solution) -0.4407^u. Also the E. M. F. of galvanic cells consist of ferrite and one of these constituents were measured in 0.5N hydrochloric acid solution at 30℃, and the following results were obtained ; graphite^+-ferrite^- 0.9810^u, graphite^+-ferrite^- (containing 0.34% Cu) 0.9535^u, Fe_3C^+-ferrite^- 0.3508^u, Fe_3C^+-ferrite^- (containing 0.34% Cu) 0.3064^u, Fe_3P^+-ferrite^- 0.2100^u, [MnS+FeS]^+-ferrite^- 0.3260^u. In the 1st and 2nd report the writer concluded that gray cast iron dissolves in a dilute hydrochloric acid mainly with the electrolytic reaction caused by local galvanic cells consist of ferrite and graphite or other noble constituents. These present experimental results gree with the former results of corrosion test as described in the previous reports.
- 社団法人日本鉄鋼協会の論文
- 1938-08-25
著者
関連論文
- 焼入油の老化について (III) : 老化防止剤に関する 2, 3 の実験
- 87 燒入油の老化について (III) : 老化防止剤に関する 2, 3 の実験(第 49 回講演大会講演大要)
- 165 GM 式焼入試験機の試作と性能について(熱処理, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 熱分解による焼入油の老化 : 焼入油の老化について V
- 77 熱分解による焼入油の老化について : 焼入油の老化について V(性質・高速度鋼, 第 57 回講演大会講演大要)
- 油の酸化重合過程と冷却能の変化 : 焼入油の老化について IV
- 16 焼入油の老化について (IV) : 油の酸化重合過程と冷却能の変化(第 53 回講演大会講演大要)
- 焼入油の老化について (II) : 礦油の老化
- 89 焼入油の老化について (II) : 礦油(日本鐵鋼協會第 47 囘講演大會講演大要)
- 水道鐵管内面の銹瘤の成因に就て
- 電弧鎔接地金の熱處理と組織の關係
- 燒入冷却劑の研究
- 焼入油の老化について (I) : 油脂の老化
- 33 燒入油の老化について (I) : 油脂の老化(日本鐵鋼協會第 46 囘講演大會講演大要)
- 焼入冷却剤の研究-7-
- 焼入冷却剤の研究(5)-動植物油(油脂)の冷却能-
- 焼入冷却剤の研究(第4報)-水及び水を主成分とする液体の冷却能-
- 焼入冷却剤の研究(6)-濃厚塩水溶液の冷却能
- 高温工具鋼の研究 (I)
- 169 軸受鋼の疲労破面について(軸受鋼・工具鋼, 性質, 日本鉄鋼協会第 88 回(秋季)講演大会)
- モリブデンの高温酸化防止コーチングの研究
- インドにおける鉄鋼製品の腐食事情とその対策
- 67 滲炭劑の老化に就ての研究 (II) : 滲炭試験による滲炭剤老化度決定(日本鐵鋼協會第 48 回講演大會講演大要)
- 66 滲炭劑の老化に就ての研究 (I) : 反応性低下に就て(日本鐵鋼協會第 48 回講演大會講演大要)
- 高クロム不銹鋼の耐酸性の研究 (II)
- 高クロム不銹鋼の耐酸性の研究 (I)
- 48 高クロム不銹鋼の耐酸性の研究 (II)(日本鐵鋼協會第 45 回講演大會講演大要)
- 亞鉛鍍金鋼板に於ける酸洗抑制劑の影響
- 耐熱鋼の加熱に依る性質の變化に就いて
- 高温工具鋼の熱処理と残留応力
- 高温工具鋼の研究 (II) : 恒温變態の研究
- 耐熱鋼の高温に於ける性質に就いて
- 鑄鐵の腐蝕現象(第三報) : 鑄鐵の腐蝕機構に關する諸實驗
- 鑄鐵の腐蝕現象(第 2 報) : 鑄鐵の腐蝕とその成分竝に組織との關係
- 16) 耐鹽酸合金の研究 (I)(日本鐵鋼協會第拾五囘講演大會)
- 21) 鑄鐵の腐蝕現象(日本鐵鋼協會第拾四囘講演大會)
- 鑄鐵の腐蝕現象(第 1 報)
- 4) 鑄鐵の腐蝕現象(第 1 報)(日本鐵鋼協會第拾壹囘講演大會)
- 耐酸鋼の探究